A kind of preparation method and application of zinc oxide high polymer

A high polymer and zinc oxide technology, which is applied in pharmaceutical formulations, dental preparations, compression molding cups, etc., can solve the problems of easy agglomeration of nano-zinc oxide and hindering application efficiency

Active Publication Date: 2022-04-29
QINGDAO UNIV OF SCI & TECH +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the characteristics of high surface energy and growth along specific crystal planes, nano-zinc oxide is very easy to agglomerate, which seriously hinders its application efficiency in rubber composites [Journal of the American Chemical Society, 2005, 127 (38 ): 13331-13337; Journal of Applied Polymer Science, 2012, 124(4): 3099-3107]

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and application of zinc oxide high polymer
  • A kind of preparation method and application of zinc oxide high polymer
  • A kind of preparation method and application of zinc oxide high polymer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A preparation method of zinc oxide polymer, comprising the following steps:

[0028] 1) In an anhydrous and oxygen-free environment, 18Kg Zn(NO 3 ) 2 ·6H 2 O was dissolved in 200L of anhydrous methanol. After complete dissolution, 0.9 Kg of urea and 39 Kg of benzyl alcohol were added to the mixture. Under nitrogen atmosphere, after stirring in the autoclave for 6 hours, the temperature was raised to 200° C. for 10 hours, and then heated to 280° C. for 5 hours to remove internal low boilers. Centrifuge to collect the dry gray powder, then calcinate to 600°C at a heating rate of 5°C / min, and then keep at 600°C for 6h to prepare nano-zinc oxide carrier particles with many defects on the surface.

[0029] 2) Add 4000g of nano-zinc oxide carrier particles prepared in step 1) and 1000g of anhydrous magnesium chloride into a dry and sealed ball mill jar replaced by high-purity nitrogen three times under a nitrogen atmosphere, and then inject 15mL of analytically pure titan...

Embodiment 2

[0032] A preparation method of zinc oxide polymer, comprising the following steps:

[0033] 1) In an anhydrous and oxygen-free environment, 18Kg Zn(NO 3 ) 2 ·6H 2 O was dissolved in 200L of anhydrous methanol. After complete dissolution, 0.9 Kg of urea and 39 Kg of benzyl alcohol were added to the mixture. Under nitrogen atmosphere, after stirring in the autoclave for 6 hours, the temperature was raised to 200° C. for 10 hours, and then heated to 280° C. for 5 hours to remove internal low boilers. Centrifuge to collect the dry gray powder, then calcinate to 600°C at a heating rate of 5°C / min, and then keep at 600°C for 6h to prepare nano-zinc oxide carrier particles with many defects on the surface.

[0034] 2) Add 4000g of nano-zinc oxide carrier particles prepared in step 1) and 1000g of anhydrous magnesium chloride into a dry and sealed ball mill jar replaced by high-purity nitrogen three times under a nitrogen atmosphere, and then inject 15mL of analytically pure titan...

Embodiment 3

[0037] A preparation method of zinc oxide polymer, comprising the following steps:

[0038] 1) In an anhydrous and oxygen-free environment, 18Kg Zn(NO 3 ) 2 ·6H 2 O was dissolved in 200L of anhydrous methanol. After complete dissolution, 0.9 Kg of urea and 39 Kg of benzyl alcohol were added to the mixture. Under nitrogen atmosphere, after stirring in the autoclave for 6 hours, the temperature was raised to 200° C. for 10 hours, and then heated to 280° C. for 5 hours to remove internal low boilers. Centrifuge to collect the dry gray powder, then calcinate to 600°C at a heating rate of 5°C / min, and then keep at 600°C for 6h to prepare nano-zinc oxide carrier particles with many defects on the surface.

[0039] 2) Add 4000g of nano-zinc oxide carrier particles prepared in step 1) and 1000g of anhydrous magnesium chloride into a dry and sealed ball mill jar replaced by high-purity nitrogen three times under a nitrogen atmosphere, and then inject 15mL of analytically pure titan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method and application of a zinc oxide high polymer. The preparation method comprises the following steps: 1) preparing a nano-zinc oxide carrier with many defects on the surface; 2) preparing an olefin polymerization catalyst: placing Nano-zinc oxide carrier and magnesium chloride are added into a ball mill tank, a titanium metal compound is injected, and the ball mill tank is put into a wet ball mill for grinding to obtain an olefin polymerization catalyst; 3) preparing a zinc oxide polymer. The zinc oxide polymer prepared by the present invention has zinc oxide active components, and the zinc oxide content can reach more than 80%. It can be used as a zinc oxide carrier to reduce the amount of ordinary zinc oxide, and can also be directly applied to gutta-percha points and medical splints and other fields.

Description

technical field [0001] The invention relates to the technical field of fine chemicals, in particular to a preparation method and application of a zinc oxide high polymer. Background technique [0002] In recent years, due to its unique optical, catalytic, piezoelectric and other physical and chemical properties, zinc oxide nanoparticles have unique photocatalytic properties, high broad-spectrum antibacterial activity, and long-term stability under extreme conditions. Biomedical fields such as sensing and detection, drug delivery, bioimaging, antibacterial, and tumor cell targeted killing have great development prospects. However, due to the strong van der Waals force between zinc oxide nanoparticles and the high surface energy caused by its high reactivity, it is easy to agglomerate, and the dispersion stability of nanoparticles is greatly reduced, which greatly limits its application in various fields. . [0003] At the same time, as an activator to accelerate vulcanizati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F136/08C08F4/02C08F4/642C08F2/44C08K3/22A61K6/71A61L31/04
CPCC08F136/08C08F4/025C08F4/022C08F4/642C08F2/44C08K3/22A61L31/04A61K6/71C08K2201/011
Inventor 曹兰郑雷臧晓燕王志晔荣先超蒲诚勇
Owner QINGDAO UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products