Composite material resistant to molten zinc corrosion and its preparation method and equipment

A composite material and zinc corrosion technology, which is applied in the field of cermet materials, can solve the problems of poor corrosion resistance of molten zinc, achieve good corrosion resistance, improve corrosion resistance of molten zinc, and be beneficial to production and application

Active Publication Date: 2022-02-15
XIANGTAN UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The embodiment of the present invention uses FeB as the hard phase, which has good corrosion resistance; W and AlFeNiCoCr are used as the bonding phase to solve the problem of poor molten zinc corrosion resistance of the bonding phase in traditional cermet materials, and improve the corrosion resistance of the material. Resistance to molten zinc corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite material resistant to molten zinc corrosion and its preparation method and equipment
  • Composite material resistant to molten zinc corrosion and its preparation method and equipment
  • Composite material resistant to molten zinc corrosion and its preparation method and equipment

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] see figure 1 , which is a schematic flowchart of a method for preparing a metal-ceramic composite material provided by an embodiment of the present invention. Specifically, the preparation method of the molten zinc corrosion-resistant composite material provided by the embodiment of the present invention includes, for example:

[0042] S11 Mix aluminum powder, iron powder, nickel powder, cobalt powder and chromium powder, and add polyethylene glycol for mechanical alloying to obtain mechanical alloying powder.

[0043] S12 vacuum drying the mechanically alloyed powder to obtain a first dry powder.

[0044] S13 Put the first dry powder into a vacuum sintering furnace for vacuum sintering, grinding and sieving to obtain AlFeNiCoCr high-entropy alloy powder.

[0045] S14 Mix the AlFeNiCoCr high-entropy alloy powder, FeB powder and W powder, add polyethylene glycol, and perform mixed ball milling to obtain a mixed powder.

[0046] S15 vacuum drying the mixed powder to ob...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
microhardnessaaaaaaaaaa
microhardnessaaaaaaaaaa
Login to View More

Abstract

The embodiment of the invention discloses a composite material resistant to molten zinc corrosion, a preparation method thereof and a device resistant to molten zinc corrosion. The composite material includes 68-78%, 10-20% and 12% FeB, W and AlFeNiCoCr. Wherein, the composition of the AlFeNiCoCr by mass percentage is: 1.96%-2.9% of aluminum powder, 24.06%-48.73% of iron powder, 17.11%-25.35% of nickel powder, 17.11%-25.35% of cobalt powder and 15.09% of chromium powder % to 22.34%. Wherein, the composite material uses FeB as the hard phase, and AlFeNiCoCr high-entropy alloy and W as the binding phase. The embodiment of the present invention uses FeB as the hard phase to have good corrosion resistance, the AlFeNiCoCr high-entropy alloy improves the brittleness of borides, the wettability between W and Zn is poor, and there is no eutectic reaction with Zn at 450 ° C, solving the problem The problem of poor molten zinc corrosion resistance of the binder phase in traditional cermet materials is solved, thereby improving the molten zinc corrosion resistance of the material.

Description

technical field [0001] The invention belongs to the field of cermet materials, and in particular relates to a composite material resistant to molten zinc corrosion, a preparation method of the composite material resistant to molten zinc corrosion and a device resistant to molten zinc corrosion. Background technique [0002] Hot-dip galvanizing is one of the most cost-effective methods for protecting metal materials such as steel from atmospheric corrosion. Hot-dip galvanized products are widely used in plates, pipes, wires, strips and hardware and electrical parts because of their excellent corrosion resistance, formability and decoration. However, molten zinc is highly corrosive to almost all single metals and most alloys. Corrosion of molten metal has always been a worldwide problem that plagues the galvanizing industry. Especially the equipment or parts immersed in the metal melt are strongly corroded and worn by the metal melt, resulting in frequent replacement of equi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/05C22C29/00C22C29/14B22F3/10B22F3/105
CPCC22C1/051C22C29/14C22C29/005B22F3/105B22F3/1007B22F2003/1051B22F2999/00B22F2201/20
Inventor 欧阳雪枚谢小龙尹付成尹冰冰王鑫铭叶平