Super-hydrophobic modification method for substance containing leather collagen fibers, tanning-agent-free tanning method and leather product

A technology of superhydrophobic modification and skin collagen, which is applied in the field of tanning, which can solve the problems of chrome tanning agent pollution, complicated process, unstable performance, etc., and achieve the improvement of shrinkage temperature and denaturation temperature, improvement of comprehensive performance, and high fiber dispersion sexual effect

Active Publication Date: 2021-07-02
SICHUAN UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the drying process of collagen fibers after absorbing water and moisture, the strong cohesive force between water molecules causes the fibers to gather and shrink, resulting in serious damage to the multi-level structure of the fiber network material.
[0005] However, due to the pollution and other problems of chrome tanning agents, if the tanning effect can be achieved without tanning agents and the performance of the finished leather can be guaranteed, the development of leather products will be greatly promoted
However, in the existing methods of tanning without tanning agents, the tanning effect is poor in durability, or the process is complicated and the performance is unstable, especially when it meets water, it is easy to return to the state of raw hide, which limits its practical use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-hydrophobic modification method for substance containing leather collagen fibers, tanning-agent-free tanning method and leather product
  • Super-hydrophobic modification method for substance containing leather collagen fibers, tanning-agent-free tanning method and leather product
  • Super-hydrophobic modification method for substance containing leather collagen fibers, tanning-agent-free tanning method and leather product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0092] The present embodiment provides the superhydrophobic modification method of the material containing skin collagen fiber, comprises the following steps:

[0093] (1) Soak the skin collagen fiber raw material in water for more than 12 hours to ensure full penetration, then add 10wt% acetic acid aqueous solution and / or 10wt% sodium bicarbonate aqueous solution to the water to adjust the pH to 6.5, and then filter the excess water. The skin collagen fibers were soaked and stirred in absolute ethanol, repeated 4 times, soaked for 2 hours each time, and then vacuum filtered to obtain skin collagen fibers with a water content of about 16.3%.

[0094] (2) Take 10 g of skin collagen fibers treated in step (1), immerse them in 100 mL of isopropanol solution containing 3 g of perfluorodecyltriethoxysilane, soak and stir at 25°C for 24 hours, and then remove by suction filtration The excess liquid was dried at 120°C for 4 hours.

[0095] (3) Wash the skin collagen fibers obtained ...

Embodiment 2

[0099] The present embodiment provides the superhydrophobic modification method of the material containing skin collagen fiber, comprises the following steps:

[0100] (1) Soak the skin collagen fiber raw material in water for more than 12 hours to ensure full penetration, then add 10wt% acetic acid aqueous solution and / or 10wt% sodium bicarbonate aqueous solution to the water to adjust the pH to 6.5, and then filter the excess water. The material containing skin collagen fibers was soaked in absolute ethanol and stirred, and repeated 4 times, soaking for 2 hours each time, and then vacuum filtered to obtain skin collagen fibers with a water content of about 16.3%.

[0101] (2) Take 10 g of skin collagen fibers treated in step (1), immerse them in 100 mL of isopropanol solution containing 1 g of octadecyltrimethoxysilane, soak and stir at 30°C for 12 hours, and then remove excess by suction filtration. Liquid, dry at 105°C for 4h.

[0102] (3) Wash the skin collagen fibers ob...

Embodiment 3

[0104] The present embodiment provides the superhydrophobic modification method of the material containing skin collagen fiber, comprises the following steps:

[0105] (1) Soak the skin collagen fiber raw material in water for more than 12 hours to ensure full penetration, then add 10wt% acetic acid aqueous solution and / or 10wt% sodium bicarbonate aqueous solution to the water to adjust the pH to 6.5, and then filter the excess water. The material containing skin collagen fibers was soaked in absolute ethanol and stirred, and repeated 4 times, soaking for 2 hours each time, and then vacuum filtered to obtain skin collagen fibers with a water content of about 16.3%.

[0106] (2) Take 12 g of skin collagen fibers treated in step (1), immerse them in 100 mL of isopropanol solution containing 2 g of hexadecyltrimethoxysilane, soak and stir for 7 hours at 35 ° C, and remove excess by suction filtration. Liquid, dry at 120°C for 4h.

[0107] (3) Wash the skin collagen fiber obtaine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
water absorptionaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of leather making, in particular to a super-hydrophobic modification method for a substance containing collagen fibers, a tanning-agent-free leather making method and a leather product. The method comprises the following steps: dipping a substance containing leather collagen fibers and having a water content of 5-20% in a liquid containing a long-chain silane coupling agent, and carrying out high-temperature treatment at 80-160 DEG C; and then conducting washing and drying. The substances containing the leather collagen fibers comprise powdery leather collagen fibers and / or pickled-disacidified bare leather obtained through treatment of a conventional leather making process; the long-chain silane coupling agent is C<n>Y<2n+1>(CH<2>)<m>SiX<3>; and the mass ratio of the substance containing the leather collagen fibers to the long-chain silane coupling agent is 1:(0.02-0.6). The leather collagen fibers treated by the method have stable super-hydrophobic performance in a wide pH range, the water antenna is higher than 150 degrees, the water absorption rate is lower than 0.8 g.g<-1>, and a complete multi-scale network structure is still kept after the leather collagen fiber is treated by water.

Description

technical field [0001] The invention relates to the technical field of leather making, in particular to a method for superhydrophobic modification of a substance containing leather collagen fibers, a method for making leather without a tanning agent, and a leather product. Background technique [0002] It has been thousands of years to make raw hide into leather, and then process it into leather products with different styles. However, the research history of leather tanning mechanism is relatively short, and there is still a lack of sufficient and detailed data. The mainstream view of traditional tanning mechanism research is that a necessary condition for tanning is that when leather is turned into leather, tanning agent molecules must interact with more than two reaction points in the collagen structure to form new crosslinks. However, the comprehensive performance of leather is not positively correlated with the crosslinking strength. Over the past few years, due to the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C14C9/00
CPCC14C9/00
Inventor 徐双凤石碧李双洋黄鑫
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap