Rotor blade integrally formed by three-dimensional woven composite material and manufacturing method thereof

A composite material, integral molding technology

Active Publication Date: 2021-07-13
TSINGHUA UNIV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using this process to make blades is complicated, and the laying of carbon fiber cloth depends on manual experience, the production efficiency is low, and it is difficult to ensure the uniformity of different blades
Moreover, since the upper airfoil, lower airfoil and the girder of the blade are only bonded together by resin, the integrity is poor, and the interlayer strength is low. It is prone to delamination damage when subjected to a large load or external impact, and cannot Give full play to the performance advantages of carbon fiber materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rotor blade integrally formed by three-dimensional woven composite material and manufacturing method thereof
  • Rotor blade integrally formed by three-dimensional woven composite material and manufacturing method thereof
  • Rotor blade integrally formed by three-dimensional woven composite material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0054] In order to more clearly illustrate the above purpose, features and advantages of the present application, specific implementation methods of the present application will be described in detail in this part with reference to the accompanying drawings. In addition to the various implementations described in this section, the present application can also be implemented in other different ways. Without departing from the spirit of the present application, those skilled in the art can make corresponding improvements, deformations and replacements. Therefore, the present application Do not be bound by the specific embodiments disclosed in this section. The scope of protection of this application should be based on the claims.

[0055] Such as Figure 1 to Figure 9 As shown, the present application proposes a three-dimensional woven composite material integrally formed rotor blade (hereinafter sometimes simply referred to as blade), which includes a root connector 1 and a bl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a rotor blade integrally formed by a three-dimensional woven composite material and a manufacturing method thereof, and the rotor blade integrally formed by the three-dimensional woven composite material comprises a root connector, wherein a plurality of rotor blades and a plurality of rotor blades, and a paddle main body which comprises the three-dimensional woven composite material formed by weaving tows, wherein the paddle main body is connected to the root connector in the mode that at least part of the tows penetrate through the tow connecting holes.

Description

technical field [0001] The application relates to a rotor blade integrally formed by three-dimensional woven composite materials and a manufacturing method thereof. Background technique [0002] At present, the rotor blades used by unmanned helicopters include upper airfoil, lower airfoil and load-bearing girder. The upper airfoil, lower airfoil and load-bearing girder need to be preformed by laying carbon fiber unidirectional cloth or woven cloth with independent molds, and then Finally, it is formed by gluing or co-curing. Using this process to make blades is complicated, and the laying of carbon fiber cloth depends on manual experience, the production efficiency is low, and it is difficult to ensure the uniformity of different blades. Moreover, since the upper airfoil, lower airfoil and the girder of the blade are only bonded together by resin, the integrity is poor, and the interlayer strength is low. It is prone to delamination damage when subjected to a large load or ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B64C27/473B64C27/48B29D99/00B64F5/10
CPCB64C27/473B64C27/48B29D99/0025B64F5/10B64C2027/4736
Inventor 王财政苏丹丹谢之峰周明
Owner TSINGHUA UNIV