Preparation method of bioactive medical dressing
A bioactive, high molecular polymer technology, applied in the field of preparation of bioactive medical dressings, can solve the problems of a large number of post-processing, complex preparation process, low production efficiency, etc., and achieve the effect of stable product, simple process and high production efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0047] This embodiment has prepared a kind of bioactive medical dressing, and specific process comprises:
[0048] Step 1, the preparation of aqueous solution
[0049] (1) Preparation of sodium alginate aqueous solution (NaA), gelatin aqueous solution (Gel) and chitosan aqueous solution (CS): sodium alginate powder and deionized water are mixed to prepare a certain concentration (preferably about 2wt%, in this implementation Example is 2wt% sodium alginate aqueous solution; gelatin powder and deionized water are mixed to prepare a certain concentration (preferably about 1wt%, the present embodiment is 1wt%) gelatin aqueous solution; chitosan powder and 1% (v / v) acetic acid is mixed, is prepared into the chitosan aqueous solution of certain concentration (preferably about 1wt%, the present embodiment is 1wt%);
[0050] (2) Platelet-rich plasma (PRP): 40 ml of blood was collected from the abdominal aorta of 10 rats, injected into a centrifuge tube containing 0.5 mmol / L EDTAK2 a...
Embodiment 2
[0058] This embodiment prepares a bioactive medical dressing, the difference from Example 1 is that in step 2, the two-channel coaxial nozzle is replaced with a three-channel coaxial nozzle with a specification of 14G / 18G / 25G (such as figure 1 a, c and c1, c2 shown). The inlet ports of the inner, middle and outer phase channels of the three-channel coaxial nozzle are respectively connected with polyethylene plastic tube ends, and the polyethylene plastic tube ends are respectively connected with the needles of the three syringes. The inner phase of the three-channel coaxial nozzle was injected with a mixed aqueous solution of gelatin (Gel) and platelet-rich plasma (PRP), the middle phase was injected with sodium alginate (NaA), and the outer phase was injected with chitosan aqueous solution (CS). like Figure 7 As shown in the blue area (in the figure, black area: cannot be spun and cannot be printed, light blue: can only be spun but not 3D printed; blue: can be spun but can ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com