Steel wire rope lubricating grease composition and preparation method thereof

A grease composition and wire rope technology, applied in the field of lubrication, can solve problems such as low dropping point, and achieve the effect of meeting the requirements of high temperature use

Pending Publication Date: 2021-11-30
CHINA PETROLEUM & CHEM CORP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing lubricating grease generally has the problem of low dropping point, so it is necessary to increase the dropping point of the wire rope lubricating grease so that it will not drip due to melting at high temperature and meet the requirements of high temperature use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel wire rope lubricating grease composition and preparation method thereof
  • Steel wire rope lubricating grease composition and preparation method thereof
  • Steel wire rope lubricating grease composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] The present invention provides a kind of preparation method of the wire rope grease composition described in the above technical scheme, comprising:

[0039] The base oil, thickener, tackifier and additives are mixed to obtain a wire rope grease composition.

[0040] In the present invention, the mixing method preferably includes:

[0041] Mix base oil, thickener and tackifier to obtain a mixture;

[0042] The mixture and additives are mixed to obtain a wire rope grease composition.

[0043] In the present invention, the mixing temperature of the base oil, thickener and tackifier is preferably 130-150°C, more preferably 135-145°C, most preferably 140°C; the mixing time is preferably 1.5-2 hours , more preferably 1.6 to 1.8 hours.

[0044] In the present invention, the mixing temperature of the mixture and the additive is preferably 90-110°C, more preferably 95-105°C, most preferably 100°C.

[0045] The steel wire rope lubricating grease composition provided by the i...

Embodiment 1

[0048] In parts by weight, add 59 parts of mineral oil (Maoming Petrochemical), 18 parts of PE wax (Nanjing Tianshi) and 23 parts of tackifier (ethylene-propylene copolymer, Lubrizol), stir and heat up to 140°C, constant temperature for 1.5~2h; after the constant temperature is over, lower the temperature to about 100°C, add 1.5 parts of diphenylamine (Xilong Chemical Test), 2 parts of T202 (zinc dialkylthiophosphate, Xinxiang Ruifeng), 2 parts of T321 ( Sulfurized isobutylene, Shenyang Feida) 1.5 parts and barium petroleum sulfonate (Suzhou Sanli) 1.5 parts, to obtain steel wire rope surface grease.

[0049] According to the following method, the steel wire rope surface grease prepared by the embodiment of the present invention 1 is tested for performance, and the test results are as follows:

[0050]

[0051]

Embodiment 2

[0053] In parts by weight, add 59 parts of mineral oil (Maoming Petrochemical), 18 parts of OPE wax (Nanjing Tianshi) and 23 parts of tackifier (ethylene-propylene copolymer, Lubrizol), stir and heat up to 140 ℃, constant temperature 1.5 ~ 2h. After the constant temperature is over, lower the temperature to about 100°C, add 1.5 parts of diphenylamine (Xilong Chemical Test), 2 parts of T202 (zinc dialkylthiophosphate, Xinxiang Ruifeng), 1.5 parts of T321 (isobutylene sulfide, Shenyang Feida) 1.5 parts and 1.5 parts of barium petroleum sulfonate (Suzhou Sanli) to obtain steel wire rope surface grease.

[0054] According to the following method, the steel wire rope surface grease prepared by the embodiment of the present invention 2 is tested for performance, and the test results are as follows:

[0055]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
drop melting pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a steel wire rope lubricating grease composition which comprises the following components, by weight: 54-65 parts of base oil, 15-25 parts of a thickening agent, 15-35 parts of a tackifier, and 1-10 parts of an additive. The steel wire rope lubricating grease with a high dropping point is obtained by optimally proportioning the types and dosages of the base oil, the thickening agent, the tackifier and the additive, and the problem that the lubricating grease drips at a high temperature is solved. The dropping point of the steel wire rope lubricating grease can reach over 95 DEG C, so that the high-temperature use requirement is met. The invention also provides a preparation method of the steel wire rope lubricating grease composition.

Description

technical field [0001] The invention belongs to the technical field of lubrication, and in particular relates to a steel wire rope lubricating grease composition and a preparation method thereof. Background technique [0002] With the development of modern industry, the operating conditions of wire ropes are becoming more and more harsh, and they need to work under high temperature conditions. Therefore, the requirements for wire rope grease are also becoming more and more stringent. However, the existing lubricating grease generally has the problem of low dropping point. Therefore, it is necessary to increase the dropping point of the wire rope lubricating grease so that it will not drip due to melting at high temperature and meet the requirements of high temperature use. Contents of the invention [0003] In view of this, the object of the present invention is to provide a steel wire rope grease composition and a preparation method thereof. The steel wire rope grease com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/00C10N50/10C10N40/32C10N30/08
CPCC10M169/00C10M2203/1006C10M2205/146C10M2205/186C10M2205/022C10M2205/024C10M2215/064C10M2223/045C10M2219/022C10M2219/044C10N2050/10C10N2040/32C10N2030/08C10N2020/02C10N2010/04
Inventor 李秀蓉康健
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap