A method for improving the seam quality of gh4151 inertial friction welding

A GH4151, inertial friction welding technology, applied in the direction of welding/welding/cutting items, manufacturing tools, measuring devices, etc., can solve the problems of welding flash fracture, flash discontinuous distribution, etc., and achieve the elimination of welding stress and temperature bearing capacity Improve and solve the effect of defects such as weld cracks

Active Publication Date: 2022-03-15
SHENYANG LIMING AERO-ENGINE GROUP CORPORATION
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention is a process improvement aimed at the crack defects existing in the welding seam of GH4151 alloy welded in the prior art, the crack at the tip of the flash extends into the base of the weld seam, the fracture of the welding flash and the discontinuous distribution of the flash

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for improving the seam quality of gh4151 inertial friction welding
  • A method for improving the seam quality of gh4151 inertial friction welding
  • A method for improving the seam quality of gh4151 inertial friction welding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A welding method for improving the weld seam quality of GH4151 alloy, comprising the steps of:

[0029] Step 1: Design the welding structure of the GH4151 alloy inertia friction welding weldment: such as figure 2 As shown, before welding, the inner and outer surfaces of the welding boss 6 and the size of the final part 8 retain a machining allowance, the outer surface retains a 2mm allowance, and the inner surface retains a 1mm allowance;

[0030] Step 2: Process the GH4151 alloy ring to the size of the welded structure, the welded outer diameter is 100mm, and the welded thickness is 8mm, such as figure 2 As shown, the roughness of the welding contact surface 7 is Ra1.6;

[0031] Step 3: Check the fit between the weldment and the tooling before welding, keep the parts in a clamped state, use alcohol to clean the welding surface, and wipe off oil and other foreign matter;

[0032] Step 4: Select the welding parameters, the welding inertia is 600kg. m 2 , Welding sp...

Embodiment 2

[0042] A welding method for improving the weld seam quality of GH4151 alloy, comprising the steps of:

[0043] Step 1: Design the welding structure of the GH4151 alloy inertia friction welding weldment, such as figure 2 As shown, before welding, the inner and outer surfaces of the welding boss 6 and the size of the final part 8 retain a machining allowance, the outer surface retains a 2.5mm allowance, and the inner surface retains a 2mm allowance;

[0044] Step 2: Process the GH4151 alloy ring to the size of the welded structure, the welded outer diameter is 250mm, and the welded thickness is 9mm, such as figure 2 As shown, the roughness of the welding contact surface 7 is Ra2.0;

[0045] Step 3: Check the fit between the weldment and the tooling before welding, keep the parts in a clamped state, use alcohol to clean the welding surface, and wipe off oil and other foreign matter;

[0046] Step 4: Select the welding parameters, the welding inertia is 800kg. m 2 , Welding ...

Embodiment 3

[0056] A welding method for improving the weld seam quality of GH4151 alloy, comprising the steps of:

[0057] Step 1: Design the welding structure of the GH4151 alloy inertia friction welding weldment, such as figure 2 As shown, before welding, the inner and outer surfaces of the welding boss 6 and the size of the final part 8 retain a machining allowance, the outer surface retains a 3mm allowance, and the inner surface retains a 2.5mm allowance;

[0058] Step 2: Process the GH4151 alloy ring to the size of the welded structure, the welded outer diameter is 400mm, and the welded thickness is 10mm, such as figure 2 As shown, the roughness of the welding contact surface 7 is Ra2.5;

[0059] Step 3: Check the fit between the weldment and the tooling before welding, keep the parts in a clamped state, use alcohol to clean the welding surface, and wipe off oil and other foreign matter;

[0060] Step 4: Select the welding parameters, the welding inertia is 1000kg. m 2 , Weldin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The patent of the present invention relates to a process method for improving the quality of GH4151 inertial friction welding seam, which belongs to the field of welding technology of GH4151 alloy used for core rotor parts and disk shaft parts of aero-engines; the process method includes three-stage pressure method of inertial friction welding , Before welding, the machining allowance is reserved for the inside and outside of the welding boss and the final part size. After the welding is completed, the flash removal and heat treatment are completed within a limited time, and the defect detection is carried out in sequence. The three-stage pressure process method can prevent the tip cracks of the welding flash from penetrating into the weld matrix and make the flash continuous. Before the welding, the machining allowance is reserved on the inside and outside of the welding boss and the final part size, which can completely remove the possible flash edge defects and ensure the final weld seam quality of the parts. The invention also utilizes different detection sequences to carry out overall quality inspection on the surface of the weld seam, the shallow surface and the inside of the weld seam, thereby effectively improving the quality of the weld seam and the level of defect detection.

Description

technical field [0001] The patent of the invention relates to the field of welding technology of GH4151 alloy used for core rotor parts of aero-engines and disk shaft parts, specifically a process method for improving the quality of GH4151 inertial friction welding seam, especially suitable for inertial friction welding where there are tip cracks in welding flash And the case where the flash is broken and the distribution is discontinuous. Background technique [0002] GH4151 alloy is a new type of structural material for aero-engines. It has excellent high-temperature performance and is regarded as a very promising aero-engine material. Since the GH4151 alloy has a high volume fraction of strengthening phase and a high content of alloying elements, problems such as cracks are likely to occur in the welding seam by using the fusion welding technology of the prior art. Inertial friction welding is a solid-phase welding technology, and its weld is a forged structure. Therefor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K20/12B23K20/24B23P15/00G01N21/64G01N27/9013G01N29/04
CPCB23K20/122B23K20/24B23P15/00G01N29/04G01N21/64G01N27/90B23K2103/08
Inventor 赵强帅焱林刘佳涛尚震祝文卉
Owner SHENYANG LIMING AERO-ENGINE GROUP CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap