Asymmetric photonic crystal film with varicoloration and its preparation method and application

A photonic crystal and angle-dependent color technology, which is applied in the field of asymmetric angle-dependent photonic crystal film and its preparation, achieves the effects of high optical change behavior, simple preparation method, and improved anti-counterfeiting ability

Active Publication Date: 2022-04-01
WUHAN UNIV OF TECH
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the currently prepared photonic crystal anti-counterfeiting patterns show a symmetrical blue shift change law with the change of viewing angle.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asymmetric photonic crystal film with varicoloration and its preparation method and application
  • Asymmetric photonic crystal film with varicoloration and its preparation method and application
  • Asymmetric photonic crystal film with varicoloration and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] (1) Fe with a particle size of 160nm 3 o 4 @PVP magnetic nanoparticles are dispersed into a mixture composed of monomer hydroxyethyl methacrylate (HEMA), crosslinker ethylene glycol dimethacrylate (EGDMA), photoinitiator 2-hydroxy-2-methyl-1-benzene In the prepolymerization liquid that hydroxyacetone (HMPP) forms, the concentration of HEMA in the prepolymerization liquid is 0.899g / mL, and the concentration of HMPP is 3.84% of monomer HEMA quality, and the concentration of EGDMA is 14.6% of monomer HEMA monomer, Fe 3 o 4The concentrations of @PVP magnetic nanoparticles are 3.12mg / ml, 6.24mg / ml, 9.36mg / ml, 12.48mg / ml, 15.60mg / ml, 18.72mg / ml respectively.

[0044] (2) Coating different Fe on the surface of the substrate 3 o 4 The pre-polymerization solution with the concentration of @PVP magnetic nanoparticles is cured with a UV lamp for 60s in a vertical uniform magnetic field of 300 Gs (the direction of the magnetic field is perpendicular to the surface of the subst...

Embodiment 2

[0047] (1) Fe with a particle size of 160nm 3 o 4 @PVP magnetic nanoparticles are dispersed into a mixture composed of monomer hydroxyethyl methacrylate (HEMA), crosslinker ethylene glycol dimethacrylate (EGDMA), photoinitiator 2-hydroxy-2-methyl-1-benzene In the pre-polymerization liquid composed of methyl acetone (HMPP), Fe 3 o 4 The concentration of @PVP is 15.60mg / ml, the concentration of HEMA is 0.899g / mL, the concentration of HMPP is 3.84% of the monomeric HEMA mass, and the concentration of EGDMA is 14.6% of the monomeric HEMA monomer.

[0048] (2) Coat the pre-polymerization liquid on the surface of the substrate, in a vertical uniform magnetic field of 300 Gs (the direction of the magnetic field is perpendicular to the surface of the substrate), and cure it with a UV lamp for 60 seconds. 90µm, 100µm, 110µm, 120µm, 130µm bottom film, in which the bottom film is embedded with a vertically arranged 1D photonic crystal structure.

[0049] figure 2 It is the spectrog...

Embodiment 3

[0051] (1) The method in Example 2 was used to prepare a bottom film with a thickness of 100 μm.

[0052] (2) The surface of the bottom layer film obtained in (1) is coated with pre-polymerization solution, and cured by a UV lamp for 60 seconds in a uniform magnetic field of the same strength inclined at 30° to the surface of the substrate to obtain thicknesses of 30µm, 40µm, and 50µm respectively. , 60µm, and 70µm top film, the bottom film is embedded with a vertically arranged 1D photonic crystal structure, and the top film is embedded with photonic crystal films of different thicknesses arranged at an angle of 30°. The thickness of the photonic crystal film The order is 130µm, 140µm, 150µm, 160µm, 170µm.

[0053] image 3 It is an actual picture of the bottom layer film with a thickness of 100 μm obtained in Example 3 during the deflection of the observation angle from -60° to 60°, taking pictures at intervals of 15° deflection.

[0054] Figure 4 It is the reflectance s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to the technical field of preparation of optical anti-counterfeiting materials, in particular to an asymmetric photonic crystal film with different colors depending on the angle and its preparation method and application. The photonic crystals arranged in the top film and the bottom film, the photonic crystal is a 1D chain structure composed of superparamagnetic nanocrystal cluster particles, the 1D chain photonic crystal in the top film is oriented obliquely to the film surface; the 1D chain photonic crystal in the bottom film The chain-like photonic crystals are oriented perpendicular to the film plane. The asymmetric color-dependent photonic crystal film of the present invention can regulate its asymmetry by changing the inclination angle between the 1D chain photonic crystal in the top film and the film surface, showing a relatively Compared with the more complex optical change behavior and higher imitation difficulty of traditional photonic crystal anti-counterfeiting labels, it can significantly improve the anti-counterfeiting ability.

Description

technical field [0001] The invention relates to the technical field of preparation of optical anti-counterfeiting materials, in particular to an asymmetric photonic crystal film with different colors depending on the angle and its preparation method and application. Background technique [0002] Photonic crystals are composed of periodic arrangements of at least two materials with different refractive indices, and their periodic lattice structures can diffract wavelengths that match visible light, thereby exhibiting bright structural colors. Compared with chemical colors based on dyes or pigments, structural colors eliminate the fading caused by photobleaching, especially without external stimuli, and can also show the characteristics of different colors, so they have great potential in the fields of anti-counterfeiting, camouflage and color display. important application prospects. [0003] At present, researchers using the angle dependence of photonic crystals have develo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B1/00
CPCG02B1/005
Inventor 马会茹李家国李刚罗巍官建国
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com