Injectable hydrogel dressing based on polyphenol-gallium ion coordination as well as preparation method and application of injectable hydrogel dressing
A technology of gallium ion and water injection, which is used in pharmaceutical formulations, medical science, bandages, etc., to achieve the effects of good tissue adhesion, good biocompatibility, and not easy to fall off
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0039] Example 1:
[0040] This embodiment provides a method of preparing an injectable hydrogel dressing based on polyphenol-gallium ion coordination, the preparation method comprising the steps of:
[0041] (1) 480 mg of chitosan is dissolved in 8 ml deionized water to give an S1 solution;
[0042] (2) 200 mg tannic acid is dissolved in 2 ml deionized water to obtain S2 solution;
[0043] (3) 30 mg of gallium nitrate is dissolved in 300 μl of deionized water to obtain S3 solution;
[0044] (4) 8 ml S1 solution, 2 ml S2 solution and 300 μl S3 solution were mixed, and stirred at 25 ° C for 1 min to mix uniform, followed by regulating the pH of the mixed solution to 7.5 with a 0.1 mol / L sodium hydroxide solution, standing for 5 min The mixed solution is adequately gel, i.e., an injectable hydrogel dressing (chitosan / tannic acid / nitrate hydrogel dressing) based on polyphenol-gallium ion coordination.
Example Embodiment
[0045] Example 2:
[0046] This embodiment provides a method of preparing an injectable hydrogel dressing based on polyphenol-gallium ion coordination, the preparation method comprising the steps of:
[0047] (1) 500 mg of sulfonated chitosan (sulfonated chitin reference document BiomarelIals, 2009, 30, 1715-1724) is dissolved in 8 ml deionized water to give an S1 solution;
[0048] (2) 100 mg of anthocyanin is dissolved in 2 ml deionized water to give an S2 solution;
[0049] (3) 50 mg of nitrate is dissolved in 300 μl of deionized water to obtain S3 solution;
[0050] (4) 8 ml of S1 solution, 2 ml S2 solution and 300 μl S3 solution were mixed, and stirred at 25 ° C for 1 min to mix uniform, then adjusted the pH of the mixed solution to 7.5 with 0.1 mol / L sodium bicarbonate solution, stand for 5 min The mixed solution is adequately gel, i.e., an injectable hydrogel dressing (sulfonated chitosan / anthocyanitritis / nitrate hydrogel dressing) based on polyphenol-gallium ion coor...
Example Embodiment
[0051] Example 3:
[0052] This embodiment provides a method of preparing an injectable hydrogel dressing based on polyphenol-gallium ion coordination, the preparation method comprising the steps of:
[0053] (1) 600 mg of chitosan is dissolved in 9 ml of deionized water to give an S1 solution;
[0054] (2) The 75 mg table did not have a supper, and the supass (EGCG) was dissolved in 1.5 ml of deionized water to give an S2 solution;
[0055] (3) 60 mg of gallium chloride was dissolved in 300 μL of deionized water to give an S3 solution;
[0056] (4) 9 ml of S1 solution, 1.5 ml S2 solution and 300 μl of S3 solution were mixed, stirred at 25 ° C for 1 min to mix uniform, then adjusted the pH of the mixed solution to 8.0 with 0.1 mol / L sodium carbonate solution. The MIN is adequately gelled, i.e., an injectable hydrogel dressing (chitosan / EGCG / chloride hydrogel dressing) based on polyphenol-gallium ion coordination.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap