Preparation method of waterborne epoxy curing agent

A water-based epoxy and curing agent technology, applied in the direction of epoxy resin coatings, coatings, etc., can solve the problems of single molecular structure, emulsification performance and curing performance to be improved, so as to enhance curing activity, emulsification effect and curing effect , to compensate for the effect of steric hindrance

Pending Publication Date: 2022-08-02
江西百盛精细化学品有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, many existing water-based epoxy curing agents have a single molecular structure, and their emulsifying and curing properties need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of waterborne epoxy curing agent
  • Preparation method of waterborne epoxy curing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The present embodiment provides a preparation method of a water-based epoxy curing agent, and the specific preparation process includes the following steps:

[0045] (1) Take 30 parts of polyetheramine M600 into a four-neck reaction flask, slowly add 12 parts of bisphenol A glycidyl ether dropwise in a nitrogen atmosphere, and then heat up to 110 °C for 4 hours to obtain polyetheramine-epoxy Additives;

[0046] (2) Take 30 parts of benzyl polyamine and 10 parts of ethylene glycol propyl ether into a four-neck reaction flask, under nitrogen atmosphere, slowly add polyetheramine-epoxy adduct, heat up to 65 ℃ and react for 4 hours, then Cool to 50°C, slowly add 18 parts of the second epoxy compound (butyl glycidyl ether) dropwise, heat up to 65°C and react for 4h, then slowly add 45 parts of water, disperse for 22min, and filter to obtain a water-based epoxy curing agent.

Embodiment 2

[0048] On the basis of embodiment 1, this embodiment also provides another second epoxy compound, and its preparation method is:

[0049] S1. After mixing oleyl alcohol polyoxyethylene ether with 14 times the amount of water, add 7 times the amount of peach wood powder to soak for 1.5h, and then evaporate the water to obtain surface-treated peach wood powder;

[0050] S2. According to the mass ratio of 0.3:1:7.5, the surface-treated peach wood powder, exo-3,6-epoxy-1,2,3,6-tetrahydrophthalic acid and toluene are placed in the reaction flask and mixed evenly , after the C12-C14 glycidyl ether and the catalyst 2-ethylhexanoate chromium were mixed uniformly, slowly dropped into the reaction flask, and stirred and refluxed for 6h in an oil bath at 105 °C, wherein the exo-3,6-epoxy The molar ratio of -1,2,3,6-tetrahydrophthalic acid, C12-C14 glycidyl ether and catalyst is 1:1.15:0.015;

[0051] S3, after the reaction finishes, filter out the peach wood powder, and the filtrate eva...

Embodiment 3

[0054] On the basis of embodiment 1, this embodiment also provides a kind of preparation method of above-mentioned benzyl polyamine:

[0055] A. Take 2,4-diaminobutyric acid, water, potassium hydroxide, and methanol into a four-necked reaction flask. Under a nitrogen atmosphere, slowly add toluene-chloride dropwise, then heat up to 60°C and react for 5h. After the reaction is completed , filtration, oil-water separation, take the organic phase, vacuum distillation;

[0056] B, the product obtained in step A is mixed with 3.5 times the amount of thionyl chloride, and the reaction is refluxed at normal temperature for 3h, while the tail gas is treated, and the obtained product is dewatered;

[0057] C, according to mass ratio 1:0.08:3, polyethylene glycol, pyridine and dichloromethane are mixed uniformly, under ice bath, stirring condition, drip the mixed solution of the product that step B obtains and dichloromethane (mass ratio is 1:3), then react for 6h, after the reaction, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a water-based epoxy curing agent, which comprises the following specific preparation processes: (1) taking polyether amine, putting the polyether amine into a four-mouth reaction bottle, slowly dropwise adding a first epoxy compound in a nitrogen atmosphere, then heating to 80-150 DEG C, and reacting to obtain a polyether amine-epoxy adduct; and (2) putting benzyl polyamine and alcohol ether into a four-mouth reaction bottle, slowly adding the polyether amine-epoxy adduct in a nitrogen atmosphere, heating to 50-80 DEG C, reacting, cooling to 40-60 DEG C, slowly dropwise adding a second epoxy compound, heating to 50-80 DEG C, reacting, slowly adding water, and dispersing for 15-30 minutes to obtain the waterborne epoxy curing agent. According to the preparation method of the waterborne epoxy curing agent provided by the invention, the emulsifying property and the curing property are improved by improving the molecular structure of the curing agent.

Description

technical field [0001] The invention belongs to the technical field of chemical coatings, and more particularly relates to a preparation method of a water-based epoxy curing agent. Background technique [0002] Waterborne epoxy resin is a kind of environment-friendly polymer material, which has many advantages such as low organic solvent content, low odor, chemical resistance, insulation and so on. It is the central development direction of epoxy resin development. At home and abroad, the research focus on water-based epoxy resin is concentrated in the field of water-based epoxy curing agent. The curing agent is water-based, that is, the curing agent is prepared into a substance that can both cure in water and emulsify epoxy. This curing agent is essentially an active emulsifier, and the use of this curing agent will not destroy the epoxy resin molecules. structure, and finally can be cured in the system, so that the prepared water-based epoxy resin retains the original pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G59/50C09D163/00
CPCC08G59/504C09D163/00
Inventor 林荣乐石孟泽曾茂权蒋玉雄
Owner 江西百盛精细化学品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap