Polylactic acid resin composition

A technology of polylactic acid resin and composition, which is applied in the field of polylactic acid resin composition, can solve the problems of brittle material performance, high price, and inability to prepare film packaging materials, etc., and achieve the effect of good flexibility and low cost

Inactive Publication Date: 2007-03-14
ZHEJIANG UNIV OF TECH
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polylactic acid resin is a new type of fully biodegradable plastic. Its raw material comes from corn, which is polymerized by fermentation, so it is also called corn plastic. Biodegradable plastics, the biggest problem in the application of polylactic acid resin at present is that the price is high, and the material performance is relatively brittle, so it cannot be used to prepare film packaging materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] According to 85 grams of polylactic acid resin, 15 grams of glycerol triacetate, and 0.1 gram of EBS, carry out the formula, melt and mix for 5 minutes in a double-roller mill, and the plasticizing temperature is 160 ° C, and the material after plasticizing is pressed in a hydraulic press to form 1.5mm flakes, the pressing temperature is 180°C; the plasticized polylactic acid obtained by pressing is tested for mechanical properties and migration. The obtained results: the tensile strength was 36.2MPa, the elongation at break was 206%, and the migration amount after 50 hours at 80°C was 1.32%.

Embodiment 2

[0018] According to the formula of 80 grams of polylactic acid resin, 20 grams of glycerol triacetate, and 0.1 grams of oleic acid amide, melt and mix for 5 minutes in a double-roller mill, and the plasticizing temperature is 160 ° C. Put the plasticized material in a hydraulic press Press into a 1.5mm sheet at a pressing temperature of 180°C; the plasticized polylactic acid obtained by pressing is subjected to mechanical property tests and migration tests. The obtained results: the tensile strength was 27.6MPa, the elongation at break was 388%, and the migration amount after 50 hours at 80°C was 3.46%.

Embodiment 3

[0020] According to the formula of 75 grams of polylactic acid resin, 25 grams of glycerol triacetate, and 0.1 grams of oleic acid amide, melt and mix in a double-roller mill for 5 minutes, and the plasticizing temperature is 160 ° C. Put the plasticized material in a hydraulic press Press into a 1.5mm sheet at a pressing temperature of 180°C; the plasticized polylactic acid obtained by pressing is subjected to mechanical property tests and migration tests. The obtained results: the tensile strength was 22.3MPa, the elongation at break was 421%, and the migration amount after 50 hours at 80°C was 5.12%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The present invention relates to one kind of polylactic acid resin composition. The polylactic acid resin composition consists of polylactic acid resin 50-85 wt%, glycecol triacetate 15-50 wt% and lubricant 0.01-1 wt%. The plasticized polylactic acid resin composition is especially suitable for making polylactic acid film, and has the features of low cost, high toughness, high tear resistance and high transparency.

Description

(1) Technical field [0001] The invention relates to a polylactic acid resin composition. (2) Background technology [0002] Polylactic acid resin is a new type of fully biodegradable plastic. Its raw material comes from corn, which is polymerized by fermentation, so it is also called corn plastic. Biodegradable plastics, the biggest problem in the application of polylactic acid resin at present is that the price is relatively high, and the second is that the material performance is relatively brittle, and film packaging materials cannot be prepared. For biodegradable plastics, disposable film packaging materials are the main fields of application. Chinese patent 03117482 increases the toughness of the polylactic acid film by adding 2-15% medical plasticizer, which is used for the growth and regeneration of soft and hard tissues in cleft palate repair. (3) Contents of the invention [0003] The purpose of the present invention is to provide a polylactic acid resin composi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/11C08L67/04
Inventor 钱欣
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap