Strengthened and toughened polypropylene composite and its preparing process

A composite material and polypropylene technology, applied in the field of polypropylene/elastomer/inorganic particle ternary composite material and its preparation, can solve problems such as the influence of processing performance and use performance, achieve simple processing operation, reduce production cost, improve cost-effective effect

Inactive Publication Date: 2003-01-15
SUN YAT SEN UNIV
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This negatively affects the processability and usability of the final product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The present invention will be further described below in conjunction with specific examples.

[0015] Table 1 and Table 2 are respectively the component distribution ratio of each embodiment of the present invention and the mechanical properties and thermal properties-crystallization behavior parameters of the product. The preparation process of each embodiment is as described above.

[0016]

[0017] The results in Table 1 show that: PP / POE / BaSO 4 The impact strength of the ternary system has been greatly improved, and the modulus and toughness have reached a better balance, which solves the problem of poor toughness of pure PP. Illustrate that the present invention makes PP / POE / BaSO with good comprehensive mechanical properties and reasonable performance-price ratio with a simple method 4 Ternary composite materials.

[0018]

[0019] Table 2 results show that: (1) BaSO 4 The three components of PP, POE, and MPOE all play a heterogeneous nuclea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A three-element composition is prepared from polypropene (PP) (72-91 wt%), POE or MPOE (1-13) and BaSO4 (7-20) through mixing, stirring, kneading and extruding out. Its advantages are high impact strength, high toughness, high P / C ratio, high resistance to thermal or ultraviolet ageing, and low cost.

Description

[0001] Technical Field The present invention relates to a polypropylene / elastomer / inorganic particle ternary composite material and a preparation method thereof. Background technique [0002] Since the 1980s, people have used elastomers and inorganic particles in the modification of polypropylene (PP) to form a ternary composite system of PP / elastomer / inorganic particles. , in order to obtain a composite material with both toughness and rigidity. Commonly used elastomers are: EPM, EPDM, SBS. The research results show that only when the content of elastomer is above 20% in these composite systems, the impact strength can be greatly improved. This reduces the performance / price ratio of the composite. CaCO in inorganic particles 3 BaSO 4 It has a toughening effect on PP, but this toughening effect can only be reflected when they are added in a large amount. This negatively affects the processability and usability of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K3/30C08L23/12
Inventor 曾汉民王坷徐布衣曾斌吴景深
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com