Stone polishing wax and method for producing the same

A production method and stone technology, applied in chemical instruments and methods, polishing compositions, etc., can solve the problems of poor wear resistance, not easy to shine, lose luster, etc., and achieve the effect of improving luminosity and color and good penetration performance.

Inactive Publication Date: 2004-01-14
王兴玺
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The previous formula used soft bright components with low melting point and low hardness, so it is easily affected by the temperature (30°C-38°C temperature), so it is not easy to show the bright effect (that is, it is not easy to shine after wiping); The grinding performance is also relatively poor, and it is easily affected by dust and loses its proper luster

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Take 12.9 kg of 80# microcrystalline wax, 5.1 kg of polyethylene wax, 5.4 kg of montan wax, 6.6 kg of SA1801# stearic acid, 49 kg of perchlorethylene and 21 kg of No. 120 solvent oil, and take another 0.04 kg of black dye and high pigment Carbon black powder 2.4 kg;

[0053] Production method: On the basis of conventional production methods in this field, heat the bright component to 120°C, and after it is completely melted, add it to the tetrachlorethylene solution that has added dye and high-pigment carbon black micropowder and stir evenly. When the temperature drops to 60°C-80°C, add aliphatic hydrocarbon compound No. 120 solvent oil, stir evenly, and when the temperature drops to 38°C-45°C, stir for another 10 minutes to prepare black glazing wax for black stone, then To pack.

Embodiment 2

[0055] Take 16.8 kg of 90# microcrystalline wax, 4.2 kg of polyethylene wax, 0.9 kg of montan wax, 8.1 kg of SA1801# stearic acid, 63 kg of perchlorethylene, 10 kg of No. 120 solvent oil, and 0.04 kg of green dye;

[0056] Production method: On the basis of conventional production methods in this field, heat the bright component to 120°C, add it into the tetrachlorethylene solution that has added green dye and stir evenly after it is completely melted, and wait until the temperature drops to 60°C- At 80°C, add aliphatic hydrocarbon compound No. 120 solvent oil, stir evenly, and subpackage when the temperature is lowered to 40°C-50°C to prepare green stone glazing wax for green stone.

[0057] Note: At 40°C-50°C, the synthesized stone glazing wax is liquid, suitable for filling, and becomes a paste-like semi-solid after the temperature drops to normal temperature.

Embodiment 3

[0059] Take 6 kg of 85# microcrystalline wax, 3.25 kg of polyethylene wax, 9.5 kg of montan wax, 6.25 kg of SA1801# stearic acid, 45 kg of tetrachlorethylene and 30 kg of No. 120 solvent oil, and 0.06 kg of red dye;

[0060] Production method: On the basis of conventional production methods in this field, heat the bright component to 120°C, add it into tetrachlorethylene and stir evenly after it is completely melted, add red dye together with tetrachlorethylene, wait for the temperature to drop When the temperature reaches 60°C-80°C, add aliphatic hydrocarbon compound No. 120 solvent oil, stir evenly, and when the temperature is lowered to 40°C-50°C, the red stone glazing wax is obtained, and then packaged.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A polishing wax for stone material features that it can effectively penetrate into porous surface of stone material, and after its volatile components including tetrachlorethylene fully volatilize its polishing component stays in the pores and on the surface of stone material for polishing the stone surface by grinding or rubbing. Its advantages are high lustre, high resistance to water, dust, harmful gas and liquid, and abrasion.

Description

technical field [0001] The technical field to which the technical solution claimed in the present invention belongs is stone glazing wax used for protective glazing of various stone materials. Background technique [0002] At present, various stone materials such as granite and marble in buildings have become important building decoration materials, and are widely used in the interior and exterior walls of buildings and the field of ground decoration. Therefore, the application of stone glazing wax is becoming more and more extensive. [0003] Porous material - stone, as a building decoration material, has many uses. Such as walls, floors, counters, furniture. Therefore, stone is often affected by external forces. Glazing wax is its protective product, and it is naturally affected by these factors. In order to protect the stone from or be less affected, as a stone glazing wax must have better resistance to external forces. [0004] There are sm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09G1/08
Inventor 王兴玺
Owner 王兴玺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com