Gold porcelain technology

A process and ceramic technology, applied in the field of craftsmanship for making special ornaments, can solve problems such as failure to achieve success, and achieve the effect of enlarged production range, simple process and lifelike patterns.

Inactive Publication Date: 2005-03-23
孙建
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For a long time, the ceramic industry has been eager to solve the manifestation of the combination of metal and ceramics, but it has not been successful

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A gold porcelain process, including tire making, thread sticking, coloring, sintering, heat preservation, and bright treatment, the manufacturing process is as follows:

[0017] 1. Tire making: ceramic materials are made into blank tires such as ceramic plates, plates or bottles according to product requirements;

[0018] 2. Filigree sticking: Use latex to fix the filigree pinched according to the pattern on the ceramic blank. According to the needs of the pattern, the filigree can use stainless steel wire and brass wire on the same product, or use stainless steel wire or brass alone Silk;

[0019] 3. Coloring: according to the design pattern, use traditional cloisonné enamel powder to dot the recesses on the surface of the blank tire;

[0020] 4. Sintering and heat preservation: Sinter in a common sintering furnace with a sintering temperature of 550°C, take out for 20 minutes, and then cool down from 550°C to room temperature in a holding furnace to release;

[0021...

Embodiment 2

[0023] A gold porcelain process, including tire making, thread sticking, coloring, sintering, heat preservation, and bright treatment, the manufacturing process is as follows:

[0024] A. Tire making: ceramic materials are made into blank tires such as ceramic plates, plates or bottles according to product requirements;

[0025] B. Filament sticking: Use adhesive to fix the filigree pinched according to the pattern on the ceramic blank. According to the pattern requirements, the filigree can use stainless steel wire and brass wire on the same product;

[0026] C. Coloring: Use traditional cloisonné enamel powder to dot the concaves on the surface of the blank according to the design pattern;

[0027] D. Sintering and heat preservation: Only one sintering is carried out in the ordinary sintering furnace, the sintering temperature is 620°C, and it is released in 25 minutes, and then it is naturally lowered from 620°C to room temperature in the holding furnace.

[0028] E. Brigh...

Embodiment 3

[0030] A gold porcelain process, including tire making, thread sticking, coloring, sintering, heat preservation, and bright treatment, the manufacturing process is as follows:

[0031] A. Tire making: ceramic materials are made into blank tires such as ceramic plates, plates or bottles according to product requirements;

[0032] B. Filament sticking: Use adhesive to fix the filigree pinched according to the pattern on the ceramic blank. According to the pattern requirements, the filigree can use stainless steel wire and brass wire on the same product;

[0033] C. Coloring: Use traditional cloisonné enamel powder to dot the concaves on the surface of the blank according to the design pattern;

[0034] D. Sintering and heat preservation: Only one sintering is carried out in the ordinary sintering furnace. The sintering temperature of the sintering and heat preservation process is 700°C, and it is released in 30 minutes, and then it is naturally lowered from 700°C to room tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Gold-like porcelain as special ornaments is products by: making formworks, binding patterned stainless steel or brass wires onto them, enameling with pigments, firing in a common furnace at 550-700 deg.C for 20-30 minutes, cooling ni a thermal keeping furnace to the amtosphere, and polishing the patterned wires. It is a metal-porcelain combined handicraft in small sizes or a large picture on wall with lively appearance and stereo visual feeling.

Description

technical field [0001] The invention relates to a process for making special decorations, in particular to a gold porcelain process in which ceramics and metals are combined. Background technique [0002] Ceramics are durable, clean and beautiful, not easy to corrode, and far cheaper than gold, silver, copper, jade, and lacquerware, and the raw materials are widely distributed and rich in reserves, so they develop rapidly. Ceramic manufacturing techniques mainly include mud refining, billet drawing, billet printing, billet sharpening, engraving, glazing, kiln firing and coloring. The performance styles of ceramics are flat hand-painted, embossed painted, decals, colored glazes, and pearl-colored effects. For a long time, the ceramic industry has been eager to solve the manifestation of the combination of metal and ceramics, but it has not been successful. Contents of the invention [0003] The object of the present inve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C1/00B44C3/00C04B41/00
Inventor 孙建
Owner 孙建
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com