Polypropylene resin for manufacturing medical syringe

A polypropylene resin and propylene technology, applied in the field of polypropylene resin, can solve the problems affecting the toughness of the material and the easy rupture of the syringe, and achieve the effects of high precipitation resistance, unique performance and stable high temperature processing performance.

Inactive Publication Date: 2005-10-05
SINOPEC SHANGHAI PETROCHEMICAL CO LTD
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the transparency of the material is generally increased by adding a nucleating agent. The turbidity of a sheet with a thickness of 1.3mm can reach 15%, but usually the addition of a nucleating agent will affect the toughness of the material. Therefore, it is currently used in the manufacture of medical syringes. The notched impact strength of polypropylene resin is about 20J / M, and the syringe made of it is easy to break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Polypropylene resin is a random copolymer of propylene and ethylene:

[0017] The ethylene content is 0.2wt%, the melting temperature is 160-165°C, and the melt flow rate is 8.0g / 10min;

[0018] Acid neutralizer:

[0019] Calcium stearate, propylene and ethylene random copolymer / calcium stearate=100 / 0.05 (weight ratio);

[0020] Antioxidant:

[0021] 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene,

[0022] Random copolymer of propylene and ethylene / 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene=100 / 0.1 (weight ratio).

[0023] Transparent nucleating agent:

[0024] Tris(3,4-dimethylbenzylidene)sorbitol,

[0025] Random copolymer of propylene and ethylene / tris(3,4-dimethylbenzylidene)sorbitol=100 / 0.2 (weight ratio).

Embodiment 2

[0027] Polypropylene resin is a random copolymer of propylene and ethylene:

[0028] The ethylene content is 0.5wt%, the melting temperature is 150-165°C, and the melt flow rate is 12g / 10min;

[0029] Acid neutralizer:

[0030] Hydrogenated talcum powder, propylene and ethylene random copolymer / hydrogenated talcum powder=100 / 0.08 (weight ratio);

[0031] Antioxidant:

[0032] Tris(2,4-di-tert-butylphenyl)phosphite,

[0033] Random copolymer of propylene and ethylene / tris(2,4-di-tert-butylphenyl)phosphite=100 / 0.1 (weight ratio).

[0034] Transparent nucleating agent:

[0035] Bis(p-methylbenzylidene)sorbitol,

[0036] Random copolymer of propylene and ethylene / bis(p-methylbenzylidene)sorbitol=100 / 0.3 (weight ratio).

Embodiment 3

[0038] Polypropylene resin is a random copolymer of propylene and ethylene:

[0039] The ethylene content is 2.9wt%, the melting temperature is 140-165°C, and the melt flow rate is 20g / 10min;

[0040] Acid neutralizer:

[0041] Hydrogenated talcum powder, propylene and ethylene random copolymer / hydrogenated talcum powder=100 / 0.10 (weight ratio);

[0042] Antioxidant:

[0043] Di-[3,3-di-(3-tert-butyl-4-hydroxyphenyl)-butyric acid]ethylene glycol ester,

[0044] Random copolymer of propylene and ethylene / di-[3,3-di-(3-tert-butyl-4-hydroxyphenyl)-butyric acid]ethylene glycol ester=100 / 0.3 (weight ratio).

[0045] Transparent nucleating agent:

[0046] Organophosphate compound NA-21

[0047] Propylene and ethylene random copolymer / organophosphate compound NA-21=100 / 0.18 (weight ratio).

[0048] The physical index of above-mentioned each embodiment polypropylene resin is listed in Table 1.

[0049] Tensile Strength

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

This invention is polypropylene resin used for making medical injector. The resin is propene and ethane atactic multipolymer, the ethane content is 0.5-5wt%. The resin contains transparent nucleating agent, acid neutralizer and antioxidant. The weigh ratios are: propene ethane atactic multipolymer / transparent nucleating agent=100 / (0.08-0.40);propene ethane atactic multipolymer / acid neutralizer=100 / (0.01-0.10); propene ethane atactic multipolymer / antioxidant=100 / (0.02-0.30). The transparent nucleating agent is sorbitol or organic phosphate compound, the acid neutralizer is one of calcium stearate or hydro-saponite or the mixture of the two, the antioxidant is one of or mixture of hindered phenol and phosphate ester. The polypropylene resin provided by this invention has good heat endurance, intension and tenacity.

Description

technical field [0001] The present invention relates to a polypropylene resin, in particular to a polypropylene resin specially used for making medical syringes. Background technique [0002] In the prior art, plastic medical syringes are generally made of polypropylene resin. According to the special application of medical syringes, the transparency and toughness of the materials used for manufacturing have high requirements. At present, the transparency of the material is generally increased by adding a nucleating agent. The turbidity of a sheet with a thickness of 1.3mm can reach 15%, but the addition of a nucleating agent will usually affect the toughness of the material. Therefore, it is currently used in the manufacture of medical syringes. The notched impact strength of polypropylene resin is about 20J / M, and the syringe made of it is relatively easy to break. Contents of the invention [0003] The invention provides a polypropylene resin used for manufacturing med...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61M5/178C08K5/521C08L23/14
Inventor 陶红陈海林刘勇董超陆国华将忠辉牟丹杨惠华高国强
Owner SINOPEC SHANGHAI PETROCHEMICAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com