Rubber compsns. for cleaning and stripping mould
A rubber composition and demoulding technology, which is applied in the field of mold cleaning and demoulding rubber compositions, can solve problems such as deterioration of the working environment, and achieve excellent demoulding force, excellent mutual solubility, and easy mixing operations
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0037]In 1000g of butadiene rubber (BR), mix and add 3 kinds of mixed detergents (monoethanolamine (MEA) 30g, N-methylpyrrolidone (NMP) 25g, dimethyl sulfoxide (DMSO) 35g), in Mixing curing agent (4,4-diperoxide tert-butyl n-butyl valerate 30g), inorganic filler (silica 300g, titanium oxide 50g), kneader and roll mill And adsorbent (Zolite X type 400g). The mixture produced in this way was put into a mold (MQFP 28×28) contaminated with epoxy molding compound (EMC), and heated at 170°C at 60kg / cm 2 The pressure is cured for 450 seconds to clean the mold. This operation is repeated until the contaminants on the mold are completely removed.
[0038] As a result, an average of 8 repeated cleaning operations can remove contaminants from the mold.
Embodiment 2
[0040] In order to confirm the effect of the cleaning catalyst, in the composition of Example 1, 5 g of KOH was added as the cleaning catalyst, and the test was performed in the same manner as in Example 1.
[0041] As a result, an average of 5 to 6 repeated cleaning operations can completely remove contaminants from the mold. This means that compared with Example 1, the washing ability is improved by about 25 to 30%.
Embodiment 3
[0043] In order to confirm the release effect, 30 g of silicone oil was further added to the composition of Example 2, and the test was performed in the same manner as in Example 2.
[0044] In Example 2, the mold was opened, and the cured rubber sheet could be grasped by hand and applied force to separate the cured rubber sheet from the mold surface. However, in this example with the addition of silicone oil, the rubber sheet was not applied with force. Next, the rubber sheet can be easily separated from the mold surface. This means that the release of the rubber sheet is greatly improved by the addition of the release agent.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap