Automatically adding concentrated wax medium for valve of motorcycle and preparation process thereof

A technology for thickening valve and motorcycle, which is applied in the fields of wax-like temperature-sensing medium for automatic thickening valve of motorcycle and its preparation, and wax-like temperature-sensing medium for wax control valve and its preparation field, which can solve the problem of unsatisfactory use. requirements and other issues, to achieve the effect of stable product performance, long service life and good use effect

Active Publication Date: 2006-11-15
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These wax temperature-sensing media are highly specific, and cannot meet the requirements when directly used in motorcycle automatic thickening valves.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automatically adding concentrated wax medium for valve of motorcycle and preparation process thereof
  • Automatically adding concentrated wax medium for valve of motorcycle and preparation process thereof
  • Automatically adding concentrated wax medium for valve of motorcycle and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) With liquid paraffin as raw material, in a distillation unit with 17 theoretical plates, at 1.33 × 10 3 Under the pressure of Pa, the distillate of 240-300°C was prepared at intervals of 5°C; under the same distillation conditions, the distillate of 300-400°C was prepared from soap wax (melting point 42.5°C). The melting point of each section fraction product is as shown in Table 1;

[0019] Fraction range

℃

Vacuum distillation product melting point

℃

Fraction range

℃

Vacuum distillation product melting point

℃

240～245

-0.7

320～325

28.4

245～250

0.6

325～330

29.6

250～255

1.9

330～335

30.6

255～260

3.3

335～340

31.8

260～265

5.0

340～345

34.1

265～270

6.9

345～350

35.3

270～275

9.0

350～355

37.6

275～280

11.0

355～360

39.7

...

Embodiment 2

[0024] (1) With liquid paraffin as raw material, in a distillation unit with 17 theoretical plates, at 1.33 × 10 3 Under the pressure of Pa, the fraction of 240-300°C was prepared at intervals of 10°C; under the same distillation conditions, the fraction of 300-400°C was prepared from soap wax (melting point 42.5°C). Each section fraction product fusing point is as shown in table 2;

[0025] Fraction range

℃

Vacuum distillation product melting point

℃

Fraction range

℃

Vacuum distillation product melting point

℃

240～250

0.1

320～330

29.2

250～260

3.0

330～340

31.5

260～270

6.2

340～350

34.5

270～280

10.1

350～360

38.5

280～290

14.1

360～370

41.5

290～300

18.0

370～380

45.2

300～310

22.1

380～390

47.5

310～320

26.5

390～400

50.0

[00...

Embodiment 3

[0030] (1) With liquid paraffin as raw material, in a distillation unit with 17 theoretical plates, at 1.33 × 10 3 Under Pa pressure, 240-300°C fractions were prepared at intervals of 20°C; under the same distillation conditions, soap wax (melting point 42.5°C) was used as raw material to prepare 300-400°C fractions. shown;

[0031] Fraction range

℃

Vacuum distillation product melting point

℃

Fraction range

℃

Vacuum distillation product melting point

℃

240～260

1.9

320～340

30.2

260～280

8.4

340～360

36.9

280～300

16.5

360～380

43.1

300～320

23.8

380～400

49.2

[0032] (2) The above-mentioned components purified by vacuum distillation are sampled in the same proportion by weight, heated and melted and mixed uniformly;

[0033] (3) Add 4% activated clay to the above mixed components at 130° C., mix for 0.5 hours and then filter to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a wax mediator which is applied to the automatic enrichment valve of the motorbike and its preparation method. It takes use of the liquid wax which contains the component of C9-C30 and soap wax as the material, and it can be prepared by the processes of vacuum distillation, mixing, refining and so on. The wax controlled valve which is prepared by this product can control the temperature during 0-50 deg.C, and the driving value of each degree is basic same. This invention can be applied to the automatic controlled part which can control the temperature during 0-50 deg.C and the driving value of which can change homogeneously as the temperature. It is especially suitable to as the temperature sensitive mediator of the automatic enrichment valve in motorbike.

Description

technical field [0001] The invention belongs to the technical field of special waxes, in particular to a waxy temperature-sensing medium for a waxy control valve and a preparation method thereof, in particular to a waxy temperature-sensing medium for a motorcycle automatic thickening valve and a preparation method thereof. Background technique [0002] The control valve using wax as the temperature-sensing medium is a self-operated valve, which uses the volume change of the wax-like temperature-sensing medium during the phase change process to control the opening of the valve so as to achieve the purpose of controlling the flow of the material flow. This kind of valve has multiple functions such as sensing, execution, feedback, and fixed value at the same time. It has temperature characteristics that do not change significantly with system pressure, high mechanical strength, good chemical stability, easy mass production and installation, low cost, and stable and reliable temp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10G73/00F16K31/68
Inventor 孙剑锋高蒿
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com