Production method of 350 MPa grade cold rolled magnetic pole steel

A production method and technology of magnetic pole steel, which are applied in the field of cold-rolled magnetic pole steel, can solve the problems of unreasonable coordination between the strength and magnetic induction intensity of cold-rolled magnetic pole steel, strict requirements for rolling equipment and process control, and unsatisfactory comprehensive quality of cold-rolled magnetic pole steel. and other problems, to achieve excellent comprehensive performance, improve plate quality, and facilitate quality control.

Inactive Publication Date: 2007-01-31
WUHAN IRON & STEEL (GROUP) CORP
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The production methods (including composition and process) of the cold-rolled magnetic pole steel disclosed in these articles have the following deficiencies: 1. The steel plate strength and magnetic induction intensity of the cold-rolled magnetic pole steel are unreasonable, and the overall quality of the cold-rolled magnetic pole steel is not ideal; 2. Strict requirements for rolling equipment and process control, high production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The production method of the steel of the present invention mainly includes several stages such as hot rolling, cold rolling and annealing.

[0036] Embodiment 1-4 of the production method of 350MPa grade cold-rolled magnetic pole steel of the present invention, the specific steps are:

[0037] (1) The slab is heated before hot rolling, the heating temperature is 1160-1230°C, and the heating and holding time is 1 hour.

[0038] (2) The step of hot rolling; the starting rolling temperature is 1050-1100°C, and the final rolling temperature is 830-890°C; the deformation process is 7 passes, and the deformation time interval of each pass is less than 0.3s, and the final billet thickness is rolled from 30mm Thin steel plates with specifications of 2.5-4.5 mm are rolled and cooled to 620-680 ° C by spraying, uniform and moderate water cooling after rolling.

[0039] (3) Air-cooling is used for cooling, and pickling is carried out when the hot-rolled steel coil is cooled belo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a process of producing 350MPa cold rolled steel magnet. It includes steps as follows: (1)to heat plate body to 1160-1230DEG C;(2)hot

Description

technical field [0001] The invention relates to a cold-rolled magnetic pole steel, especially a production method of a cold-rolled magnetic pole steel with a yield strength of 350MPa. Background technique [0002] In order to solve the problem of energy shortage in our country, the country has increased investment in hydropower projects, and the number of hydropower facilities under construction, expansion and reconstruction has increased significantly. Among the special key new materials for large hydropower units, the magnetic pole steel plates used in the rotors of generator sets Demand has also increased significantly. [0003] The magnetic pole steel plate of the rotor of the generator set must have sufficient strength to meet the safety of the hydro-generator; in order to reduce the eddy current loss of the unit, the magnetic pole steel plate must have better magnetic flux than the yoke steel plate; the magnetic pole is made of laminated steel plates, In order to ensu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/14C21D8/12C21D11/00B21B37/00
Inventor 刘浩刘家宁钟定忠胡吟萍孙方义彭涛鄢檀力孔勇江余晓静黎静
Owner WUHAN IRON & STEEL (GROUP) CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com