Method for producing thermal-formation products of plastic sheet material

A technology of a plastic sheet and a production method, which is applied to the production field of plastic sheet thermoforming products, can solve the problems of high printing cost, complicated printing process, easy to contaminate food, etc., and achieves low printing cost, simple pattern printing process, and avoidance of Effects of contaminated food

Active Publication Date: 2007-04-18
广东日烽吸塑包装实业有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional production method of plastic sheet thermoforming products is generally to print the pattern after the product is thermoformed, which has the following problems: 1. Due to the uneven shape of the blow-molded product or the blister product, it is not possible to use ordinary printing technology on the blow-molded product or Printing on the surface of blister products can only use a special printing process, so the printing process is complicated and the printing cost is high; 2. The pattern printing layer is located on the surface of the product, making the printed pattern layer easy to wear, fall off, and fade. When printing food, the printed pattern layer is also easy to contaminate the food

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing thermal-formation products of plastic sheet material
  • Method for producing thermal-formation products of plastic sheet material
  • Method for producing thermal-formation products of plastic sheet material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] This embodiment adopts blow molding process (positive pressure molding process) to manufacture plastic cups, as shown in Fig. is m, and the column distance is n; the production method of this embodiment comprises the following main steps in turn: (1), on one side of the transparent plastic film 2, a plurality of plum blossom patterns 21 are printed, and the patterns are divided into multiple groups. The number of plum blossom patterns is equal to the number of cavities in the blow mold, which is 12. The patterns 21 of each group are distributed into two rows and six columns. The row spacing of the patterns in each group is correspondingly equal to the row spacing m of the cavity in the mold. The column distance of pattern in each group is correspondingly equal to the column distance n of each mold cavity in the mould, as shown in Figure 2; The position of the group of printed patterns constitutes a corresponding relationship (in this embodiment, this corresponding relat...

Embodiment 2

[0021] This embodiment adopts the plastic-absorbing process (vacuum negative pressure forming process) to manufacture plastic handicrafts. The main steps of this embodiment are basically the same as those in Embodiment 1, except that this embodiment adopts the plastic-absorbing process to form, and the cavities in the mold are only arranged in a row. Each group of patterns printed in the plastic film is also distributed in a row, and the horizontal spacing of the patterns in each group corresponds to the horizontal spacing of each cavity in the mould; and an opaque plastic sheet is used to compound with a transparent plastic film. The plastic product that this embodiment obtains is plastic handicraft 5, and the shape of its center is close to tortoise shell shape, and as shown in Figure 5, the tortoise shell shape center position is printed with pattern.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A thermally shaping method for preparing the product from plastic sheet includes such steps as printing patterns and locating marker on transparent plastic film, attaching the plastic film onto surface of a plastic sheet, heating the plastic sheet for softening it, moving it into a moulding cavity, applying pressure to make it close to the inner surface of moulding cavity, cooling, demoulding and punch shearing.

Description

technical field [0001] The invention belongs to a method for producing plastic products, in particular to a method for forming plastic products with concave-convex shapes through thermoforming of plastic sheets. Background technique [0002] Plastic sheets can be thermoformed to make thermoformed products, including blow molded or blistered products. Plastic sheet thermoforming adopts blow molding process or blister process. The blow molding process or the blister process is to heat the plastic sheet to soften it, and then use positive pressure air or vacuum negative pressure to make the plastic sheet adhere to the inner wall of the mold cavity to form a concave-convex shape blow molding product or blister product. Some plastic sheet thermoformed products need to be printed with patterns or characters. The traditional production method of plastic sheet thermoforming products is generally to print the pattern after the product is thermoformed, which has the following proble...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C51/10B29C51/46B29C51/14B29C51/26B29B11/04
Inventor 许小飞
Owner 广东日烽吸塑包装实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap