Aluminium strip for capacitor shell

A technology for aluminum strips and capacitors, applied in capacitors, electrical components, furnace types, etc., can solve the problem that the requirements of the punching process cannot be guaranteed, and achieve moderate tensile strength, good comprehensive mechanical properties, and small ear rate. Effect

Active Publication Date: 2007-06-06
JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Aluminum is the main material for the shell of electrolytic capacitors. With the development of the electronics industry, the demand for electrolytic capacitors, the main electronic components, is also increasing. At present, the shells of capacitors at home and abroad are mainly made of 1060 alloy aluminum strips. The process plan Cast-rolling, cold-rolling, and finished product annealing are followed in sequence, and the temperature is 250-350°C. However, the aluminum strips for capacitor shells made of this brand of aluminum have blackened surfaces after punching, and the ear-making rate during processing and forming is generally between More than 3.5%, can not guarantee the shell punching process requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0006] Embodiment 1: The raw material adopts the aluminum material of 1100 alloy, and its weight composition is: Al: 99 parts; Fe: 0.53 parts; Si: 0.18 parts; Mn: 0.05 parts; Zn: 0.10 parts; After smelting, casting and rolling, one cold rolling to 6mm, the homogenized annealing temperature is 620°C for 15 hours, the second cold rolling is to 2.5mm, and the intermediate annealing temperature is 450°C for 10 hours; three times cold rolling to the thickness of the finished product is 0.35mm, the annealing temperature of the finished product is 240°C, lasts for 20 hours, and then it is made by cutting and packaging processes. In the prior art, the process and process parameters of capacitor aluminum strips produced with 1060 grade aluminum as raw materials are different.

Embodiment 2

[0007] Embodiment 2: The raw material adopts 1100 grades of aluminum, and its weight components are: Al: 99.09 parts; Fe: 0.49 parts; Si: 0.15 parts; Mn: 0.05 parts; Zn: 0.10 parts; After smelting, casting and rolling, one cold rolling to 5mm, the homogenized annealing temperature is 590°C for 15 hours, the second cold rolling is to 1.0mm, and the intermediate annealing temperature is 500°C for 10 hours; three times cold rolling to the thickness of the finished product is 0.26mm, the annealing temperature of the finished product is 210°C, lasts for 20 hours, and then it is made by cutting and packaging processes. In the prior art, the process and process parameters of capacitor aluminum strips produced with 1060 grade aluminum as raw materials are different.

Embodiment 3

[0008] Embodiment 3: The raw material adopts 1100 grades of aluminum, and its weight components are: Al: 99.02 parts; Fe: 0.51 parts; Si: 0.17 parts; Mn: 0.05 parts; Zn: 0.10 parts; After smelting, casting and rolling, one cold rolling to 3mm, the homogenized annealing temperature is 550°C for 15 hours, the second cold rolling is to 2.0mm, and the intermediate annealing temperature is 550°C for 10 hours; three times cold rolling to the thickness of the finished product is 0.28mm, the annealing temperature of the finished product is 180°C, lasts for 20 hours, and then it is made by cutting and packaging processes. In the prior art, the process and process parameters of capacitor aluminum strips produced with 1060 grade aluminum as raw materials are different.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The aluminum strip for capacitor shell is produced through smelting, casting and rolling, the first cold rolling, homogeneous annealing at 550-620 deg.c, the secondary cold rolling, the middle annealing at 450-550 deg.c, the third cold rolling, product annealing at 180-240 deg.c and other technological steps. The material alloy contains Al 99-99.09 weight portions, Fe 0.49-0.53 weight portions, Si 0.15-0.18 weight portions, Mn 0.05 weight portions, Zn 0.10 weight portions, and Cu 0.12-0.15 weight portions. The aluminum strip has moderate tensile strength, high elongation, low earing rate and high comprehensive mechanical performance.

Description

Technical field [0001] The invention relates to an aluminum strip material for capacitor shells. Background technique [0002] Aluminum is the main material for the shell of electrolytic capacitors. With the development of the electronics industry, the demand for electrolytic capacitors, the main electronic components, is also increasing. At present, the shells of capacitors at home and abroad are mainly made of 1060 alloy aluminum strips. The process plan Cast-rolling, cold-rolling, and finished product annealing are followed in sequence, and the temperature is 250-350°C. However, the aluminum strips for capacitor shells made of this brand of aluminum have blackened surfaces after punching, and the ear-making rate during processing and forming is generally between More than 3.5%, can not guarantee the shell punching process requirements. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the invention provides an aluminum strip mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P23/04C22C21/00C21D9/52H01G2/10
Inventor 刘倜刘文彬
Owner JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap