Middle layer material of composite floor with superior toughness and preparation method thereof

A composite floor, a superior technology, applied in the middle layer material of composite floor and its preparation field, can solve the problems of high shrinkage rate and expansion rate, low toughness, unguaranteed quality, etc., and achieve the effect of reducing expansion rate and shrinkage rate

Active Publication Date: 2016-09-21
ZHEJIANG KINGDOM NEW MATERIAL GRP CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing composite flooring generally has shortcomings such as low product toughness, high shrinkage rate and expansion rate. In the actual production and use process, these determinations lead to relatively poor quality of the product, and the quality cannot be guaranteed, thus making the product relatively low in cost performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The middle layer material of composite flooring with excellent toughness described in this embodiment is composed of PVC, plasticizer, stabilizer, calcium carbonate and nitrile rubber containing acrylonitrile, wherein the mass parts of each component are: PVC100 parts, 36 parts of plasticizers, 2 parts of stabilizers, 510.6 parts of calcium carbonate, 7 parts of nitrile rubber containing acrylonitrile; the content of acrylonitrile in the described nitrile rubber is 31%;

[0015] The stabilizer is a calcium-zinc composite stabilizer;

[0016] The order number of described calcium carbonate is 325 orders;

[0017] A preparation method for the middle layer material of composite flooring with superior toughness, the PVC powder, plasticizer and stabilizer of the formula are placed in the mixing equipment and mixed for 15 minutes; then calcium carbonate is added and mixed for 15 minutes again to make Stir fully and mix evenly; finally add nitrile rubber and mix again for 15 ...

Embodiment 2

[0019] The middle layer material of composite flooring with excellent toughness described in this embodiment is composed of PVC, plasticizer, stabilizer, calcium carbonate and nitrile rubber containing acrylonitrile, wherein the mass parts of each component are: PVC100 parts, 36 parts of plasticizers, 2 parts of stabilizers, 510.6 parts of calcium carbonate, 7 parts of nitrile rubber containing acrylonitrile; the content of acrylonitrile is 33% in the described nitrile rubber;

[0020] The stabilizer is a calcium-zinc composite stabilizer;

[0021] The order number of described calcium carbonate is 325 orders.

Embodiment 3

[0023] The middle layer material of composite flooring with excellent toughness described in this embodiment is composed of PVC, plasticizer, stabilizer, calcium carbonate and nitrile rubber containing acrylonitrile, wherein the mass parts of each component are: PVC100 parts, 36 parts of plasticizers, 2 parts of stabilizers, 510.6 parts of calcium carbonate, 7 parts of nitrile rubber containing acrylonitrile; the content of acrylonitrile in the described nitrile rubber is 35%;

[0024] The stabilizer is a calcium-zinc composite stabilizer;

[0025] The order number of described calcium carbonate is 325 orders.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of composite floor production, in particular to a composite floor middle layer material with superior toughness, which consists of 100 parts by mass of PVC, 36 parts of plasticizer, 2 parts of stabilizer, 510.6 parts of calcium carbonate, and acrylonitrile-containing 7 parts of nitrile rubber; the content of acrylonitrile in the nitrile rubber is 31-35%; the preparation method of the middle layer material of the composite floor with superior toughness, the PVC powder of formula quantity, plasticizer, stabilizer are placed Mix and stir in the mixing equipment for 15 minutes; add calcium carbonate and mix and stir again for 15 minutes to make it fully stir and mix evenly; finally add nitrile rubber and mix and stir again for 15 minutes, so that the materials are mixed evenly. The shrinkage rate of the middle layer material of the composite floor obtained by the method is less than or equal to 0.03%, the expansion rate is less than or equal to 0.1%, and its hardness can reach 65°.

Description

technical field [0001] The invention relates to the field of composite floor production, in particular to a composite floor middle layer material with superior toughness and a preparation method thereof. Background technique [0002] Existing composite flooring generally has shortcomings such as low product toughness, high shrinkage rate and expansion rate. In the actual production and use process, these determinations lead to relatively poor quality of the product, which cannot be guaranteed, thus making the product relatively low in cost performance. Contents of the invention [0003] The object of the present invention is to provide a composite floor middle material with excellent toughness and its preparation method in order to solve the deficiencies of the above-mentioned technologies. advantage. [0004] In order to achieve the above object, the middle layer material of the superior toughness designed by the present invention is composed of PVC, plasticizer, stabili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L9/02C08K3/26
Inventor 戴会斌
Owner ZHEJIANG KINGDOM NEW MATERIAL GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com