Paste for back contact-type solar cell

a solar cell and back contact technology, applied in the direction of sustainable manufacturing/processing, final product manufacturing, conductors, etc., can solve the problems of preventing low-cost production, time-consuming and complex production process, and lowering so as to improve efficiency and economic benefits, reduce the risk of reducing the power generation efficiency of the cell, and improve the effect of electrical characteristics

Inactive Publication Date: 2008-09-25
EI DU PONT DE NEMOURS & CO
View PDF5 Cites 91 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0016]Electrodes formed using the paste of the present invention have low contact resistance with the solar cell semiconductor.
[0017]In addition, the paste of the present invention is able to form p-type electrodes having superior electrical characteristics by applying onto a p-type semiconductor and firing. Moreover, the electrodes can be formed by a thick film p...

Problems solved by technology

In the case of solar cells, however, high-temperature treatment results in the risk of lowering the power generation efficiency of the cell.
In addition, in the case of the application of thin films technique, the production pro...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paste for back contact-type solar cell
  • Paste for back contact-type solar cell
  • Paste for back contact-type solar cell

Examples

Experimental program
Comparison scheme
Effect test

examples

[0068]Although the following provides an explanation of the present invention through examples thereof, the present invention is not limited to these examples.

(I) Preparation of Silver Pastes

[0069]Silver pastes 1 and 2 were produced to have the compositions shown in Table 1 using the materials indicated below.

[0070](i) Silver Particle

[0071]Flaked silver particle [d50 2.7 μm (as determined with a laser scattering-type particle size distribution measuring apparatus)

(ii) Glass Frit

[0072]Leaded: Lead borosilicate glass frit

[0073]Components: SiO2 / PbO / B2O3 / ZnO

[0074]Softening point: 440° C.

[0075]Lead-free: Lead-free bismuth glass frit

[0076]Components: SiO2 / Al2O3 / B2O3 / ZnO / Bi2O3 / SnO2

[0077]Softening point: 390° C.

(iii) Resin

[0078]Ethyl cellulose resin (Aqualon, Hercules)

(iv) Solvent

[0079]Terpineol

TABLE 1(Parts bySilverGlass fritweight)particleLeadedLead-freeResinSolventTotalPaste 170.305.252.5021.95100.00Paste 270.305.252.5021.95100.00

[0080]The silver particle, glass frit, resin and solvent ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Temperatureaaaaaaaaaa
Electrical resistanceaaaaaaaaaa
Electrical resistanceaaaaaaaaaa
Login to view more

Abstract

Disclosed is a paste for a back contact-type solar cell that includes: (a) electrically conductive particles containing silver particle and added particles selected from the group consisting of (i) metal particles selected from the group consisting of Mo, Tc, Ru, Rh, Pd, W, Re, Os, Ir and Pt particles, (ii) a metal alloy containing the metal particles, and (iii) particles loaded with the metal particles, (b) glass frit, and (c) a resin binder.

Description

BACKGROUND OF THE INVENTION[0001]1. Field of the Invention[0002]The present invention relates to a paste for a solar cell, and more particularly, to an electrically conductive paste used to form electrodes of a back contact-type solar cell.[0003]2. Technical Background[0004]Silver paste is widely used for the electrode paste used in solar cells, since electrode pastes for solar cells are required to have low electrical resistance to facilitate improved efficiency. In the case of contact between a metal and semiconductor, a Schottky barrier is known to be formed that causes a considerable increase in contact resistance. This type of contact is referred to as Schottky contact. Since the electrical resistance of an electrode is the sum of the conductor resistance and contact resistance, in addition to lowering the conductor resistance of an electrode paste, it is also necessary to reduce the contact resistance with the conductor. The ideal contact of an electrode material, free of a Sc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L31/0224H01B1/02
CPCC03C8/04C03C8/10C03C8/18C03C14/006C03C2214/08Y02E10/547H01B1/22H01L31/022433H01L31/022441H01L31/03529H01L31/1804C03C2214/16Y02P70/50
Inventor AKIMOTO, HIDEKI
Owner EI DU PONT DE NEMOURS & CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap