A preparation method, a red technology, is applied in the preparation field of medium-temperature ceramic red glaze, which can solve the problems of large amount of lead discharge, the amount of toxic substances dissolved and reduced discharge of red ceramic glaze, and the difficulty of getting involved in tableware or children's products, etc., so as to achieve smooth hand feeling , good smoothness and thermal stability, uniform and pure color effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] A method for preparing a medium-temperature bright red glaze is characterized in that: the medium-temperature bright red glaze contains the following components by weight percentage:
[0026] Potassium feldspar 20%; Quartz 13%;
[0027] Calcite 10%; Calcined Zinc Oxide 0.5%;
[0028] Longyan washing mud 3.5%; transparent frit 5%;
[0029] Barium carbonate 1%;
[0030] water 42%;
[0031] Scarlet material 5%;
[0032] The preparation method of the above-mentioned bright red glaze is as follows:
[0033] Take potassium feldspar, quartz, calcite, calcined zinc oxide, Longyan washing mud, transparent frit, barium carbonate in the components according to the above weight percentage; mix and grind for 21 hours, and the fineness reaches 325 mesh; sieve; then group The quantity is required to add water and mix thoroughly, then increase the red material and mix thoroughly.
Embodiment 2
[0035] A method for preparing a medium-temperature bright red glaze is characterized in that: the medium-temperature bright red glaze contains the following components by weight percentage:
[0036] Potassium feldspar 15%; Quartz 20%;
[0037] Calcite 7%; Calcined Zinc Oxide 2%;
[0038] Longyan washing mud 5%; transparent frit 3%;
[0039] Barium carbonate 2%;
[0040] Water 41%;
[0041] Scarlet material 5%;
[0042] The preparation method of above-mentioned scarlet glaze is the same as embodiment 1.
Embodiment 3
[0044] A method for preparing a medium-temperature bright red glaze is characterized in that: the medium-temperature bright red glaze contains the following components by weight percentage:
[0045] Potassium feldspar 22%; Quartz 11%;
[0046] Calcite 6%; Calcined Zinc Oxide 2.5%;
[0047] Longyan washing mud 0.5%; transparent frit 4%;
[0048] Barium carbonate 3%;
[0049] Water 41%;
[0050] Scarlet material 10%;
[0051] The preparation method of above-mentioned scarlet glaze is the same as embodiment 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap