Combined pretreatment method of wood cellulose and system thereof

A lignocellulose and pretreatment technology, which is applied in fiber raw material processing, textile and papermaking, etc., can solve the problems of low hydrolysis rate of hemicellulose, low lignin removal rate, large power cost consumption, etc. Conversion rate, cellulose enzymatic hydrolysis conversion rate reduction, the effect of reducing enzyme dosage

Inactive Publication Date: 2009-12-02
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the hemifiber hydrolysis rate of dilute acid warm roasting method is also not high (70%~80%), and lignin removal rate is low, and the reaction time of dilute acid warm roasting method is longer, and power cost consumption is too large, and longer The reaction time causes the sugar monomers to further produce fermentation inhibitors such as furfural, formic acid, acetic acid, and hydroxymethylfurfural, which affect subsequent enzymatic hydrolysis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combined pretreatment method of wood cellulose and system thereof
  • Combined pretreatment method of wood cellulose and system thereof
  • Combined pretreatment method of wood cellulose and system thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Air-dried corn stalks (moisture 12.82%, benzene alcohol extract 17.44%, cellulose 40.08%, hemicellulose 20.03%, lignin 19.95%, ash content 5.52%) are pulverized into 40 mesh particles through universal pulverizer 19, then Load dilute acid circulation device 10 from feed port 12, open valve 1, valve 2, inject 0.8% dilute H from acid storage tank 15 2 SO 4 In the reactor, corn stover and dilute H 2 SO 4 The solid-liquid ratio is 1:10; open valve 3, valve 4, close valve 1, valve 2, start circulation pump 9, flow rate is set to 10L / min, liquid level is positioned at the upper end of filter plate 13 during reaction, at 95 ℃ Circulation reaction for 4 hours, during the reaction, the liquid part is circulated through the filter plate 13, the solid material part is blocked by the filter plate 13 and left in the reactor, and the liquid part passes through the pump 9 and then returns to the reactor by spraying the spray head 14 Middle; after the reaction finishes, close valve ...

Embodiment 2

[0028] Air-dried corn stalks (12.82% of moisture, 17.44% of benzene alcohol extract, 40.08% of cellulose, 20.03% of hemicellulose, 19.95% of lignin, 5.52% of ash content) are pulverized into 50 mesh particles through universal pulverizer 19, and then Load dilute acid circulation device 10 from feed port 12, open valve 1, valve 2, inject 0.8% dilute H from acid storage tank 15 2 SO 4 In the reactor, corn stover and dilute H 2 SO 4 The solid-liquid ratio is 1:10; open valve 3, valve 4, close valve 1, valve 2, start circulation pump 9, flow rate is set to 10L / min, liquid level is positioned at the upper end of filter plate 13 during reaction, at 90 ℃ Circulation reaction for 4 hours, during the reaction, the liquid part is circulated through the filter plate 13, the solid material part is blocked by the filter plate 13 and left in the reactor, and the liquid part passes through the pump 9 and then returns to the reactor by spraying the spray head 14 Middle; after the reaction ...

Embodiment 3

[0030] Air-dried corn stalks (12.82% of moisture, 17.44% of benzene alcohol extract, 40.08% of cellulose, 20.03% of hemicellulose, 19.95% of lignin, 5.52% of ash content) are pulverized into 50 mesh particles through universal pulverizer 19, and then Load dilute acid circulation device 10 from feed port 12, open valve 1, valve 2, inject 0.98% dilute H from acid storage tank 15 2 SO 4 In the reactor, corn stover and dilute H 2 SO 4 The solid-liquid ratio is 1: 6; Open valve 3, valve 4, close valve 1, open nitrogen valve 18, pass into N from nitrogen cylinder 17 2 , pressurize to 2.5MP, start the circulation pump 9, set the flow rate to 10L / min, the liquid level is located at the upper end of the filter plate 13 during the reaction, and circulate the reaction at 105°C for 2h, the liquid part circulates through the filter plate 13 during the reaction, and the solid Part of the material is blocked by the filter plate 13 and left in the reactor, and the liquid part passes throug...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a combined pretreatment method of lignocellulose. Lignocellulose is pulverized and loaded into a circulation reactor, and dilute acid is injected, and the circulation pump is turned on to carry out a circulation reaction at a temperature of 50°C to 200°C. The reaction After the end, the obtained hydrolyzate is deacidified and used for fermentation; after the remaining lignocellulose in the circulation reactor is washed, it is put into a ball mill and added with lye for ball milling. After the ball milling is completed, it is used for subsequent enzymatic hydrolysis. The invention can effectively improve the conversion rate of hemicellulose in lignocellulose, the removal rate of lignin, the conversion rate of cellulose enzymolysis, and reduce the fermentation inhibitory products. Concentration, and the water consumption of pretreatment can be set according to the needs of subsequent fermentation concentration.

Description

technical field [0001] The invention belongs to the field of chemical industry, and in particular relates to a method and system for pretreatment of lignocellulose by combining dilute acid circulation and alkaline ball milling. Background technique [0002] Lignocellulose pretreatment refers to the use of chemical and physical methods to separate its three components, cellulose from lignin and hemicellulose. At the same time, the internal hydrogen bonds of cellulose are opened to become amorphous cellulose, some glycosidic bonds are broken, the degree of polymerization is reduced, hemicellulose is hydrolyzed into monosaccharides such as xylose and arabinose, and the subsequent enzymatic hydrolysis efficiency is improved. [0003] The current pretreatment methods include concentrated acid method, dilute acid warm baking method, alkali treatment method, sulfur dioxide method, peroxide method, steam explosion method, ammonia fiber explosion method, carbon dioxide explosion meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21C5/00
Inventor 黄和严立石张红漫黄之初贾红华陈敬文林增祥高振
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com