Soft solder for stainless steel braze welding

A technology of solder and stainless steel, applied in the direction of welding/cutting medium/material, welding medium, welding equipment, etc., can solve the problems of weakened corrosion resistance, poor wetting, and poor spreading performance, so as to improve corrosion resistance and improve Good wetting and spreading performance, good welding performance

Inactive Publication Date: 2010-03-03
浙江天力久田管业有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the existing commercially available solder is used for soldering, it has the disadvantages of poor wetting and spreading properties, and weakened corrosion resistance of the welded joint, especially the joint area between the solder and the base metal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soft solder for stainless steel braze welding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] This embodiment is a solder for stainless steel brazing, and its proportion is: 1.0 Cu, 1.0% Ni, 0.001% Li, 0.001% Ti, and the rest is Sn; all percentages are mass percentages. The relevant data of this embodiment are shown in Table 1.

Embodiment 2

[0020] This embodiment is a solder material for stainless steel brazing, and its proportion is: 6.0% Cu, 0.01% Ni, 0.2% Li, 0.1% Ti, and the rest is Sn; all percentages are mass percentages. The relevant data of this embodiment are shown in Table 1.

Embodiment 3

[0022] This embodiment is a solder for stainless steel brazing, and its proportion is: 3.0% Cu, 0.1% Ni, 0.1% Li, 0.05% Ti, and the rest is Sn; all percentages are mass percentages. The relevant data of this embodiment are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a soft solder used in stainless steel brazing. The ratio of the solder comprises 1.0-6.0 wt percent of Cu, 0.01-1.0 wt percent of Ni, 0.001-0.2 wt percent of Li, 0.001-0.1 wt percent of Ti and the rest is Sn. All the percentages are mass percentage. The product in the invention is especially applicable to stainless steel brazing and has the advantages that no inter granularcorrosion occurs among the stainless steels and the welding effect is better.

Description

technical field [0001] The invention belongs to the technical field of solder, and in particular relates to a solder. Background technique [0002] Brazing means that when the operating temperature is lower than the base metal but higher than the melting temperature of the solder, the solder melts into liquid metal while the base metal remains solid, and the liquid solder wets and capillary flows in the gap or on the surface of the base metal , filling, spreading, interacting with the base metal, and forming a firm connection after cooling. It is characterized by small deformation of the workpiece, precise size after welding, and sometimes it can even be "seamless" without processing. Commonly used in brazing of precision parts in aerospace, satellite, radar, electronics and other industries. Brazing includes brazing and soft soldering. Brazing with a solder whose melting temperature is below 450°C is called soldering, and the above is called brazing. Correspondingly, sol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/26C22C13/00
Inventor 阮继成
Owner 浙江天力久田管业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap