Heat-resistance type transfer aluminum plated paper and its producing process

A production process and aluminized paper technology, applied in papermaking, paper coating, physical treatment of paper, etc., can solve the problems of affecting the appearance of cigarette pack packaging, deterioration of light reflectivity, discoloration, etc., and achieve natural degradation, good indicators, and coating layer leveling effect

Inactive Publication Date: 2007-10-10
SHAOGUAN DONGYANGGUANG PACKAGE PRINTING CO LTD
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the temperature resistance limitation of the selected coating for ordinary temperature-resistant transfer aluminized paper, when the OPP film is heat-sealed, the heat of the heat-sealed part will pass through the coating composed of the release layer and the bonding layer, making the coating The molecular configuration of the resin changes, resulting in rheology and destruction, which in turn causes air and heat to penetrate into the resin layer, resulting in deterioration of light reflectivity and discoloration, which greatly affects the appearance of cigarette packs and other product packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Release liner, formulate coated coatings in the following weight ratios:

[0022] Resin: cellulose acetate butyl resin 85%

[0023] Nitrocellulose resin 15%

[0024] Solvent: Butanone 48%

[0025] Diacetone Alcohol 20%

[0026] Ethyl acetate 22%

[0027] Isopropanol 10%

[0028] Resin accounts for 10% by weight of coating;

[0029] Tie coat, formulate the applied coating in the following weight ratios:

[0030] Resin: Acetate butyl cellulose resin 25%

[0031] Nitrocellulose resin 65%

[0032] Acrylic resin 5%

[0033] Alkyd 5%

[0034] Solvent: Butanone 48%

[0035] Diacetone Alcohol 20%

[0036] Ethyl acetate 22%

[0037] Isopropanol 10%

[0038] Resin accounts for 13% by weight of coating;

[0039] Then add 1% coloring material relative to the weight percentage of the binding layer coating and mix it evenly for subsequent use;

[0040] Use a release layer coating to coat the PET film once (inc...

Embodiment 2

[0047] For the release layer, prepare a one-coat coating in the following weight ratios:

[0048] Coating: Acetate butyl cellulose resin 75%

[0049] Nitrocellulose resin 22%

[0050] Acrylic resin 3%

[0051] Solvent: Butanone 48%

[0052] Diacetone Alcohol 20%

[0053] Ethyl acetate 22%

[0054] Isopropanol 10%

[0055] Resin accounts for 9% by weight of coating;

[0056] Tie coat, formulate the applied coating in the following weight ratios:

[0057] Resin: Acetate butyl cellulose resin 25%

[0058] Nitrocellulose resin 75%

[0059] Solvent: Butanone 48%

[0060] Diacetone Alcohol 20%

[0061] Ethyl acetate 22%

[0062] Isopropanol 10%

[0063] Resin accounts for 12% by weight of coating;

[0064] The PET film is coated once with the above-mentioned release layer coating (including leveling and drying), and the dry coating amount is 0.6g / m 2 , use the bonding layer coating on the release layer for secondary...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thermal resistanceaaaaaaaaaa
glossaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a temperature-resistant type transfer aluminized paper and its production process. Said process successively includes the following steps: coating release layer on the film; coating anchoring layer on release layer; vacuum aluminizing on the anchoring layer; coating adhesive on the aluminized layer; then making them be combined with paper; stripping film from release layer so as to obtain the invented temperature-resistant type transfer aluminized paper.

Description

technical field [0001] The invention relates to a composite material, more specifically, the invention relates to an aluminized paper-based composite material and a production process thereof. Background technique [0002] The aluminum-paper composite material produced by the vacuum aluminum-plating transfer method has a strong metallic texture although it uses less aluminum; it has strong light-shielding, temperature-insulating, and moisture-proof properties, and can replace pure aluminum foil, aluminized film and other composite products. And it is suitable for subsequent processing with printing machines, embossing machines, high-speed cross-cutting machines and other machines. Therefore, in recent years, it has been used as a new type of environmentally friendly packaging material in the packaging industry at home and abroad, such as being widely used in cigarettes, food, medicine and other packaging. field. [0003] Existing vacuum aluminized transfer method produces a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/08D21H21/50D21H25/06D21H19/84
Inventor 潘安庆郝潮转郭辉喻荣稳张东彬
Owner SHAOGUAN DONGYANGGUANG PACKAGE PRINTING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap