Nylon/acrylonitrile-butadiene-styrene resin mixing material

A technology of styrene resin and butadiene, which is applied in the field of blended materials, can solve the problems of material heat resistance decline and achieve good heat resistance, low density and good fluidity

Active Publication Date: 2008-01-16
CHONGQNG PRET NEW MATERIAL +2
View PDF2 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method also has the problem of seriously reducing the heat resistance of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4 and comparative example 1

[0034] Dry nylon 6 resin 2, ABS-2, S-MI-MAH resin (comparative example 1-2 does not add S-MI-MAH resin) and antioxidant 1098 by the embodiment in table 1 in parts by weight 1 to implementation 4 and the composition ratio of comparative example 1 is mixed, wherein

Embodiment 1

[0036] PA6-2: 55 ABS-2: 30 S-MI-MAH: 15 Antioxidant 1098: 0.1

Embodiment 2

[0038] PA6-2: 65 ABS-2: 25 S-MI-MAH: 10 Antioxidant 1098: 0.1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a nylon/acrylonitrile-butadiene-styrene resin blending material, which comprises the component of nylon, ABS resin, antioxidant and graft compatibilizer. The invention is characterized in that the graft compatibilizer is styrene-N- phenyl maleimide- maleic anhydride copolymer. The components are counted by weight: nylon 50 to 80 portions, the ABS resin 10 to 35 portions, the styrene-N- phenyl maleimide- maleic anhydride copolymer 4 to 15 portions and the antioxidant 0.1 portion. The nylon/acrylonitrile-butadiene-styrene resin blending material of the invention has the advantages of low density, good fluidity, fine hear resistance, chemical resistance and mechanical property, which can be used for making inner decorative parts, and used as the material for making an air exhaust grill and a defroster grill of a vehicle, vehicle door components and a motorcycle baffle.

Description

technical field [0001] The invention relates to a blend material, in particular to a blend material composed of nylon (PA), acrylonitrile-butadiene-styrene ternary copolymer resin (ABS) and a graft compatibilizer. Background technique [0002] Nylon, that is, polyamide resin, not only has excellent mechanical properties, but also has excellent chemical resistance, good self-lubricating properties and flexibility, so it is widely used in various fields, such as various auto parts, electric tools Housings, e-commerce equipment parts, sporting goods, and more. However, at the same time, nylon also has disadvantages such as poor notched impact performance and poor dimensional stability, which limits its further application space. In order to improve these shortcomings of nylon, people have done many improvements. Among these tasks, a commonly used method is to mix nylon and various rubbers. At the same time, in order to fully integrate nylon and rubber, corresponding compatibi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L55/02C08L51/00
Inventor 陈永东朱江磊张祥福周文
Owner CHONGQNG PRET NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka