Technique for regenerating waste solvent paint
A technology of waste solvent and process, which is applied in the field of waste solvent paint regeneration process, can solve the problems of waste of resources and other problems, and achieve the effect of high pass rate and scientific and reasonable regeneration method
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] Example 1. A regeneration process for waste solvent paint, the steps are as follows:
[0027] (1) Classify the waste solvent paint after coating construction according to its base material composition and color, and then put the waste solvent paint of the same composition and color in the flash tower, and fractionally distill the high polarity paint with a distillation range within 150 °C The solvent is stored in a tank for later use; the residue is filtered through a 40-mesh screen to remove impurities to obtain waste paint;
[0028] (2) drop the waste paint of the same hue of step (1) gained in the jacketed distillation still, drop into solvent simultaneously, the weight ratio of waste paint and solvent is 1: 0.05; Then the material in the still is heated, When the temperature of the material reaches 40°C, start the agitator in the distillation kettle to stir, stop heating and stirring when the temperature of the material reaches 100°C, keep it warm for 1 hour, and d...
Embodiment 2
[0032] Example 2. A regeneration process for waste solvent paint, the steps are as follows:
[0033] (1) Classify the waste solvent paint after coating construction according to its base material composition and color, and then put the waste solvent paint of the same composition and color in the flash tower, and fractionally distill the high polarity paint with a distillation range within 150 °C The solvent is stored in a tank for later use; the residue is filtered through a 60-mesh sieve to obtain waste paint;
[0034] (2) drop the waste paint of the same hue of step (1) gained in the jacketed distillation still, drop into solvent simultaneously, the weight ratio of waste paint and solvent is 1: 0.15; Then the material in the still is heated, When the temperature of the material reaches 60°C, start the agitator in the distillation kettle to stir, stop heating and stirring when the temperature of the material reaches 120°C, keep it warm for 4 hours, and distill the moisture i...
Embodiment 3
[0038]Example 3. A regeneration process for waste solvent paint, the steps are as follows:
[0039] (1) directly take the waste paint of the same hue from the manufacturing industry and put it into a jacketed still, and simultaneously put in a solvent. The weight ratio of the waste paint to the solvent is 1:0.05; then heat the material in the still, and when the material After the temperature reaches 40°C, start the agitator in the distillation kettle to stir, stop heating and stirring when the temperature of the material reaches 100°C, keep it warm for 1 hour, and distill the water in the material through the tube condenser at the same time; until no water is distilled Start stirring again, open the valve to discharge the material, and pass through a 60-mesh sieve to obtain paint material A, and save the filter residue A separately;
[0040] (2) paint material A is put into ball mill, start ball mill 2 hours, shut down, drop into the highly polar solvent of step (1) gained, ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap