Flexible flat cable

A flat cable and flexible technology, applied in the field of flexible flat cables, can solve the problems of corrosive gas generation, plasticizer precipitation, etc., and achieve the effect of excellent electrical insulation

Inactive Publication Date: 2008-05-07
SUMITOMO ELECTRIC IND LTD
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of flexible polyvinyl chloride resin, in addition to the danger of corrosive gas and dioxins being generated if incinerated, may also precipitate plasticizers after disposal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flexible flat cable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0093] Using a twin-shaft mixer (45 mm φ, L / D = 42), melt-mix the components with the mixing formula shown in Example 1 in Table 1, melt-extrude in the form of strands, and then cool and cut the melted strands to make small pellets . In the resin composition described in Table 1, in 100 parts by weight of the resin component, 0.5 part by weight of oleic acid amide is mixed as a lubricant, and 1 part by weight of tetrakis [3-(3,5-bis tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester.

[0094] Eight flat conductors (flat tinned copper wires) with a width of 1.2 mm and a thickness of 0.15 mm are fed from the supply bobbin group to the concentrator, and arranged in parallel at a conductor pitch of 2.0 mm. Then, the eight flat conductors arranged in parallel were conveyed to a mold of a melt injection molding machine, and small pellets of the resin composition shown in Example 1 in Table 1 were supplied from the melt injection molding machine for insulating coating. T...

Embodiment 2～8

[0097] Each flexible flat cable was produced in the same manner as in Example 1, except that the mixing recipe of the flame-retardant resin composition in Example 1 was changed to that shown in Examples 2 to 8 in Table 1. The results are shown in Table 1.

[0098] Table 1

[0099] Example

1

2

3

4

5

6

7

8

TPU

(1) Adipate type TPU JIS hardness = A80

(2)PTMG type TPU JIS hardness=A80

(3) PC type TPU JIS hardness = A80

(4)PTMG type TPU JIS hardness=A85

(5) PC type TPU JIS hardness = A85

(6) Adipate type TPU JIS hardness = A85

(7) Adipate type TPU JIS hardness = A97

(8)PTMG type TPU JIS hardness=A98

EVA

(9) EVA-1 VA=90wt%

(10) EVA-2 VA=50wt%

(11) EVA-3 VA=41wt%

metal hydroxide

(12) Synthetic magnesium hydroxide

(13) Natural Magnesium Hydroxide

(14)Organic peroxide

(15) Cross-linking assistant

- ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
tensile strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

A flexible flat cable is provided to facilitate division or branching into a plurality flexible flat cables with a predetermined number of straight angle conductors by including cutting grooves on both surfaces of an insulating coating along a longitudinal direction. A flexible flat cable(10) is formed by insulating coating of a plurality of straight angle conductors(11) arranged in parallel with an insulating coating material(12) at once. The insulating coating material is composed of a flame-retardance resin composition including a resin component 100 parts by weight and a metal hydroxide 40~250 parts by weight. The resin component includes a thermoplastic polyurethane elastomer with a JIS hardness of below A97 measured according to JIS K 7311 and an ethylene acetic vinyl copolymer with an acetic vinyl unit 50~90 wt% at a ratio of 40:60 to 90:10.

Description

technical field [0001] The present invention relates to a flexible flat cable which is formed by integrally insulating and overmolding a plurality of flat conductors arranged in parallel with an insulating coating material. Specifically, it relates to a flexible flat cable which does not contain Insulation coating material of halogen flame retardant, has high flame retardancy, and excellent mechanical properties, heat resistance, heat aging resistance, heat deformation resistance, low temperature characteristics (flexibility at low temperature), and electrical insulation . Background technique [0002] Insulated wires or shielded wires, insulated cables and other insulation-coated wires, the conductors of which are insulated and coated with insulating coating materials. In insulation-coated electric wires, flame retardancy is generally required in addition to insulation. Therefore, as an insulation coating material for insulation coating electric wires used for in-device w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B7/08H01B7/04H01B7/295H01B3/42H01B3/44C09K21/00
CPCH01B3/30H01B7/04H01B7/0838H01B7/295
Inventor 新地敦大川裕之森内清晃早味宏山崎智
Owner SUMITOMO ELECTRIC IND LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap