1942 results about "Organic peroxide" patented technology

A golf ball includes a hot-molded product of a rubber composition comprising a base rubber composed of (a) 20-100 wt % of a polybutadiene having a high cis-1,4 content, a minimal 1,2 vinyl content, and a viscosity η of up to 600 mPa·s at 25° C. as a 5 wt % toluene solution, and satisfying a certain relationship between Mooney viscosity and polydispersity index Mw/Mn, in combination with (b) 0-80 wt % of another diene rubber, (c) an unsaturated carboxylic acid, (d) an organosulfur compound, (e) an inorganic filler, (f) an organic peroxide, and optionally, (g) an antioxidant. The hot-molded product has a difference in JIS-C hardness between the center and surface thereof of up to 15 units. The composition and hardness characteristics of the hot-molded product provide the golf ball with a solid comfortable feel upon impact and an excellent rebound.

An anisotropic conductive adhesive contains conductive particles dispersed in a resin composition, wherein the resin composition includes a radical polymerization resin (A), an organic peroxide (B), a thermoplastic elastomer (C) and a phosphoric ester (D). The resin composition can further contain an epoxy silane coupling agent (E) represented by formula (2) or (3). The resin composition is mixed with other components after the radical polymerization resin (A), the thermoplastic elastomer (C), the phosphoric ester (D) and the epoxy silane coupling agent (E) are reacted. It is also possible to preliminarily react only the phosphoric ester (D) and the epoxy silane coupling agent (E) and to react the product of the preliminary reaction with the radical polymerization resin (A) and the thermoplastic elastomer (C), and then to add other components. The anisotropic conductive adhesive of the present invention can be used for electrical joining of electronic or electric parts of electrical apparatus.

A golf ball has a cover member and a core member. The cover member contains: 3 to 30 parts by weight of a thermoplastic elastomer containing polyamide; 5 to 50 parts by weight of a terpolymer ionomer containing ethylene, (meth)acrylic acid, and (meth)acrylic ester; 30 to 80 parts by weight of a copolymer ionomer containing ethylene and (meth)acrylic acid; and 1 to 20 parts by weight of an epoxidized-diene-based block copolymer. The core member is formed by vulcanizing a rubber composition containing: 100 parts by weight of a base rubber, A parts by weight of an alpha, beta-unsaturated carboxylic acid or a metal salt thereof, B parts by weight of an organic peroxide, and C parts by weight of a sulfide where A, B, and C satisfies the relationship:andA lies in the range from 25 to 45.

The invention discloses a radiation pre-crosslinked ethylene-vinyl acetate (EVA) resin film which comprises the following components in parts by weight: 51-99.58 parts of EVA resin, 0.3-2 parts of organic peroxide crosslinking agent, 0.01-5 parts of assistant crosslinking agent, 0.1-2 parts of antioxidant, 0.01-2 parts of silane coupling agent, 0-40 parts of pigment and 0-40 parts of polyolefin elastomer. The invention also discloses a preparation method of the radiation pre-crosslinked EVA resin film, which comprises the steps of sufficiently mixing 51-99.58 parts of EVA resin, 0.3-2 parts of organic peroxide crosslinking agent, 0.01-5 parts of assistant crosslinking agent, 0.1-2 parts of antioxidant, 0.01-2 parts of silane coupling agent, 0-40 parts of pigment and 0-40 parts of polyolefin elastomer, and adding into an extruder; extruding and forming a film through a T-shaped flat mould; rolling and radiating to obtain the radiation pre-crosslinked EVA resin film. Since the film is partially crosslinked before use, the dimensional stability and heat resistance of the film are remarkably improved, thus the film is suitable for large-scale popularization and application.

An encapsulating material for solar cell containing a laminated adhesive and heat resistant layer (A) and a buffering layer (B), wherein a difference in flexural modulus between the heat resistant layer (A) and the buffering layer (B) is at least 30 MPa or more, is provided. The adhesive and heat resistant layer (A) is preferably an olefin polymer (a) having a melting point (according to JIS K7121) of 75° C. or higher and having a storage elastic modulus at 150° C. of 10³ Pa or more and the buffering layer (B) is preferably an olefin polymer (d) having a stiffness of 100 MPa or less. The encapsulating material for solar cell can provide superior transparency, flexibility, heat resistance and adhesiveness and can remarkably improve production efficiency of a solar cell module even when no organic peroxide is used. The encapsulating material can also exhibit a performance capable of corresponding to the thickness reduction of the solar cell element even when an organic peroxide is used. A solar cell module containing the encapsulating material is also provided.

A moisture curable polyolefin composition comprising:(a) a polyolefin, and for each 100 parts by weight of component (a),(b) 0.1 to 10 parts by weight of an unsaturated alkoxy silane;(c) 0.01 to 2 parts by weight of an organic peroxide;(d) 0.01 to 2 parts by weight of a silanol condensation catalyst;(e) 0.02 to 2 parts by weight of a hindered amine stabilizer;(f) 0.01 to 1 part by weight of a hindered phenol antioxidant; and(g) 0.01 to 1 part by weight of an arylamine antioxidant.

A multi-piece solid golf ball has a solid core obtained by molding and vulcanizing a rubber composition which includes (A) a base rubber containing a polybutadiene synthesized using a rare-earth catalyst, (B) an unsaturated carboxylic acid and/or a metal salt thereof, (C) an organic sulfur compound, (D) an inorganic filler and (E) an organic peroxide. The core is enclosed within a mantle of one or more layer which is made primarily of a thermoplastic resin and has a Durometer D hardness of 30 to 70. The mantle is enclosed within a cover which is made primarily of a thermoplastic polyurethane and which has a Durometer D hardness of 40 to 60 that is lower than the Durometer D hardness of the outermost layer of the mantle. This construction provides the golf ball with an outstanding rebound.

Compositions are disclosed which comprise mixtures of at least one compound selected from silicone elastomers, bis-, tri- or higher polymaleimides and/or bis-, tri- or higher polycitraconimides, and at least one compound selected from p-phenylene-diamine based antiozonants, sulfur compounds capable of accelerating sulfur vulcanization of polymers capable of being crosslinked by sulfur and polysulfide polymers which when compounded into polymers curable by free radical initiators in the presence of free radical initiators permit substantially tack free surface cure of the polymers by decomposition of the free radical initiator in the presence of molecular oxygen. Compositions containing the above ingredients and at least one free radical initiator, curable compositions containing the combination and processes for making and using the compositions are also disclosed.

An improved oxidative process that employ a robust, non-aqueous, and oil-soluble organic peroxide oxidant for effective desulfurization and denitrogenation of hydrocarbons including petroleum fuels, hydrotreated vacuum gas oil (VGO), non-hydrotreated VGO, petroleum crude oil, synthetic crude oil from oil sand, and residual oil. Even at low concentrations and without the assistance of catalysts, the non-aqueous organic peroxide oxidant is extremely active and fast in oxidizing the sulfur and nitrogen compounds in the hydrocarbon feedstocks. Furthermore, the process generates a valuable organic acid by-product that is also used internally as the extractive solvent for effective removal of the oxidized sulfur and nitrogen from the hydrocarbons without the need of a final adsorption step. Novel process steps are also disclosed to substantially prevent yield loss in the oxidative process.

A novel process for modification of polyolefines and their copolymers thereof, enables the production of modified PP with minimal deterioration of molecular weight and low gel content PE and their copolymers and with minimal yellowness. The novel compound is comprised of polyolefin resin or a mixture of resins, unsaturated acidic monomer and organic peroxide, together with low volatility polar acrylic co-monomer and low softening point resin, in a continuous reactive reactor The novel process minimizes sublimation of maleic anhydride and improves distribution of monomers and initiator prior to the melting of the polyolefin.

It is possible to manufacture a highly reliable image display device capable of proceeding with resin cure even in the case where a protective panel is provided with a light shielding portion.

A liquid crystal display unit 2 having a liquid crystal display panel 8 and a light transmissive protective panel 3 having a light shielding portion 5 are disposed face to face, a resin composition 10 is interposed between the liquid crystal display unit and the protective panel, and the resin composition is cured into a cured resin layer 11. As the resin composition 10, a light-heat-curing resin composition and containing a photopolymerization initiator and organic peroxide of thermal polymerization initiator is used. In curing the resin composition 10, cure by light (ultraviolet rays) irradiation is performed until a cure ratio of the resin composition becomes 30% or more and thereafter thermal cure is performed.

The present invention provides a process for producing an encapsulating material for solar cell which makes high-speed crosslinking possible and causes no blister phenomenon without significant restrictions being imposed on the conditions for molding the encapsulating material.

The present invention provides a process for producing the encapsulating material for solar cell including impregnating a molded form of an ethylene copolymer with an organic peroxide in a liquid state at normal temperature which shows a decomposition temperature (a temperature at which the half-life period is one hour) of not higher than 150° C.

A process for producing the encapsulating material for solar cell in which dialkyl peroxide (A) and an organic peroxide (B) selected from peroxycarbonate and peroxyketal at a ratio by weight of 10/90 to 90/10 of (A) and (B) in a liquid state impregnate the molded form of the ethylene copolymer is a preferable embodiment of the present invention.

A composition comprising: (a) polyethylene; (b) as a scorch inhibitor, [1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione]; (c) a thioester; (d) a hindered amine stabilizer; and (e) an organic peroxide.

The present invention relates to biodegradable polymer compositions comprising poly(lactic acid) and poly(epsilon caprolactone) mixed with organic peroxide and magnesium silicate minerals. In addition, the present invention relates to films, coatings and products made on the basis of said compositions and to a method for their preparation.

The invention relates to the field of composite materials, in particular to a continuously-directional glass fiber reinforcement unsaturated polyester sheet molding compound. The continuously-directional glass fiber reinforcement unsaturated polyester sheet molding compound comprises the following components in part by weight: 15 to 50 parts of unsaturated polyester resin, 5 to 12 parts of low astringent, 8 to 20 parts of chopped glass fibers of 12 to 26 millimeters, 1.5 to 8 parts of directional continuous glass fibers, 10 to 50 parts of calcium carbonate, 10 to 50 parts of aluminum hydroxide, 0.2 to 1 part of organic peroxide, 1 to 4 parts of styrene, 0.2 to 1 part of thickening agent, and 1 to 3 parts of mold discharging agent. The continuously-directional glass fiber reinforcement unsaturated polyester sheet molding compound has the advantages of reasonable formula design, good flame retardance, high strength, low manufacturing cost and stable quality.

The invention provides an ethylene vinyl acetate (EVA) adhesive film used for solar battery packaging. The adhesive film comprises the following components in part by mass: 100 parts of ethylene vinyl acetate, 0.01-4 parts of organic peroxides, 0.01-3 parts of cross-linking aid, 0.01-3 parts of silane coupling agent, 0.1-1 part of light stabilizing agent, 0-1 part of ultraviolet light absorbing agent and 0.0001-0.01 part of fluorescent whitening agent. The invention also provides a solar battery assembly which comprises the ethylene vinyl acetate adhesive film. The EVA adhesive film is not easy to produce air bubbles when the solar battery assembly is laminated. Both the EVA adhesive film and the solar battery assembly have excellent heat and humidity resistance, ageing resistance and ultraviolet aging resistance.

A composition comprising:(a) polyethylene;(b) as a first antioxidant, a thiobisphenol;(c) as a second antioxidant, a compound containing 3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate in the molecule;(d) as a third antioxidant, distearyl thiodipropionate; and(e) an organic peroxide,with the proviso that each antioxidant is present in an amount of about 0.01 to the about 0.2 part by weight and the organic peroxide is present in an amount of about 0.5 to about 3 parts by weight, all per 100 parts by weight of polyethylene.

The present invention relates to a pneumatic tire with a built-in sealant layer having a color other than black. The sealant layer is derived from a sealant precursor layer comprised of a butyl rubber, organoperoxide and silica together with a colorant. The butyl rubber-based precursor sealant layer is built into the tire to form a tire assembly and its butyl rubber component is depolymerized during a subsequent curing of the tire at an elevated temperature in a suitable mold to form the tire having the resultant built-in colored sealant layer. The sealant precursor composition may additionally contain clay and/or calcium carbonate.