Metal refiner for magnesium alloy and preparation method thereof

A refiner and magnesium alloy technology, applied in the field of metal material processing, can solve the problems of large size of magnesium strontium compound, poor refining effect of magnesium alloy, unstable strontium content, etc., to achieve no environmental pollution, low production cost, fine Strong chemical effect

Inactive Publication Date: 2008-07-30
CHANGSHU NANJING NORMAL UNIV DEV RES INST
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strontium content in the Mg-Sr alloy produced by this method is unstable, which leads to the unstable quantity of the magnesium-strontium compound used for nu...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal refiner for magnesium alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A metal refiner for magnesium alloys, the refiner is based on magnesium, contains strontium, neodymium and lanthanum, the mass percentage of alloy elements is: Sr 5%, Nd 0.3%, La 0.3%, and the rest is magnesium 94.4% , the 0.1μm submicron magnesium-strontium compound phase is distributed on the alloy matrix.

Embodiment 2

[0011] A metal refiner for magnesium alloys, the refiner is based on magnesium, contains strontium, neodymium and lanthanum, the mass percentage of alloy elements is: Sr 30%, Nd 0.6%, La 0.6%, and the rest is magnesium 68.8% , the submicron magnesium-strontium compound phase of 0.8 μm is distributed on the alloy matrix.

Embodiment 3

[0013] A metal refiner for magnesium alloys, the refiner is based on magnesium, contains strontium, neodymium and lanthanum, the mass percentage of alloy elements is: Sr20%, Nd0.5%, La0.5%, the rest is magnesium79%, Submicron magnesium-strontium compound phases of 0.5 μm are distributed on the alloy matrix.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a metal refiner for a magnesium alloy and is characterized in that the refiner adopts magnesium as the basal body and contains strontium, neodymium and lanthanum elements. The mass percentage for the alloy elements is as follows: Sr more than or equal to 5 percent and less than or equal to 30 percent, Nd more than or equal to 0.3 percent and less than or equal to 0.6 percent, La more than or equal to 0.3 percent and less than or equal to 0.6 percent and the rest is magnesium. The submicron phases of the magnesium strontium compound with a length of 0.1 to 0.8 micrometer are distributed on the basal body of the alloy. The refiner preparing method of the invention has simple technique, stable elements, no environmental pollution and low manufacturing cost. The refiner obtained from the method has an excellent service effect, which has a refining effect is 3 to 5 times of that of a common refiner under the same adding condition.

Description

1. Technical field [0001] The invention belongs to the technical field of metal material processing, and in particular relates to a metal refiner for magnesium alloys and a preparation method thereof, specifically a metal refiner for magnesium alloys containing a submicron magnesium-strontium compound phase and a preparation method thereof. 2. Background technology [0002] Existing technology: At present, due to the light weight of magnesium alloy, it has higher specific strength and specific stiffness than other alloys. However, the tensile strength of magnesium alloys does not have an absolute advantage compared with other alloys, and one of the most effective ways to improve the strength and toughness of magnesium alloys is to refine the grains of magnesium alloys by using a refiner, such as using Sr-containing metals. Refining agent to refine the grains of magnesium alloys. The role of Sr is to form magnesium-strontium compounds, which serve as the basis for the nuclea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C23/00C22C1/06
Inventor 王玲赵浩峰姚以俊谢爱根李庆芳雷勇赵学余
Owner CHANGSHU NANJING NORMAL UNIV DEV RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap