Method for producing and preparing artificial jade
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and technology of jade, which is applied in the field of building decoration materials, can solve the problems of yellowing and discoloration, unstable quality, and unsatisfactory decorative effects, etc.
Inactive Publication Date: 2008-08-13
金纪德
View PDF0 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The artificial jade and similar products produced by the existing technology have poor strength and wear resistance, which affects the service life of the product, poor transparency, gloss, anti-oxidation, and anti-ultraviolet ability, and will turn yellow, discolor and become brittle after a long time of use Even cracks will affect the appearance of the product, the quality is unstable, the effect is not realistic compared with natural jade, the transparency and gloss of jade are not achieved, and the decorative effect is not ideal
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
example 1
[0032] Unsaturated resin 70-100%
[0033] Gel coat resin 0-10%
[0034] Aluminum hydroxide 0-30%
[0035] Accelerator 0.1-1.2%
[0036] Curing agent 0.2-1.6%
[0037] Flame retardant 0.1-2%
[0038] Coupling agent 0.1-2%
[0039] Defoamer 0.1-2%
[0040] Antioxidant 0.01-2%
[0041] Light stabilizer 0.1-2%
[0042] Color paste 0.01-10%
[0043] Luminous powder 0.1-10%
[0044] Glitter powder 0.1-5%
example 2
[0046] Unsaturated resin 70-100%
[0047] Gel coat resin 0-10%
[0048] Aluminum hydroxide 0-30%
[0049] Accelerator 0.1-1.2%
[0050] Curing agent 0.2-1.6%
[0051] Flame retardant 0.1-2%
[0052] Coupling agent 0.1-2%
[0053] Defoamer 0.1-2%
[0054] Antioxidant 0.01-2%
[0055] Light stabilizer 0.1-2%
[0056] Color paste 0.01-10%
example 3
[0058] Unsaturated resin 70-100%
[0059] Gel coat resin 0-10%
[0060] Aluminum hydroxide 0-30%
[0061] Accelerator 0.1-1.2%
[0062] Curing agent 0.2-1.6%
[0063] Flame retardant 0.1-2%
[0064] Coupling agent 0.1-2%
[0065] Defoamer 0.1-2%
[0066] Antioxidant 0.01-2%
[0067] Light stabilizer 0.1-2%
[0068] Color paste 0.01-10%
[0069] Luminous powder 0.1-10%
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a method for producing man-made jade, using polyester resin as main ingredient, hydrafil as filler and accelerator, using curing agent, flame retardant, coupling agent, defoamer, antioxidant, light stabilizer, color paste, noctilucence powder, flash powder as auxiliary material, wherein the materials can be used at one time and can choose several kinds to use, thereby having flexibility. Production steps are as follows: 1, coating demoulding wax on the surface of a mould, 2, painting a well-prepared gel coat resin with a brush on the surface of the mould, 3, stirring evenly the materials in proportion, 4, pouring the mixxed materials to the mould, 5, vacuumizing in a vacuum-pumping room, 6, solidifying, 7, demoulding, 8, polishing, 9, polishing and waxing, 10, making out the product. The product has the advantages of luxury style, realistic jade, rich color, high permeability, smooth surface, wearing resistance, hard, scale resistance, anti-ultraviolet, simple production, easy implementation.
Description
technical field [0001] The invention belongs to the field of building decoration materials, and relates to the production and preparation method of artificial jade. Background technique [0002] The artificial jade and similar products produced by the existing technology have poor strength and wear resistance, which affects the service life of the product, poor transparency, gloss, anti-oxidation, and anti-ultraviolet ability, and will turn yellow, discolor and become brittle after a long time of use As a result, cracks will affect the appearance of the product, the quality is unstable, and the effect is not realistic compared with natural jade, the transparency and gloss of jade have not been reached, and the decorative effect is not ideal. Contents of the invention [0003] The purpose of the present invention is to make up for the above deficiencies, to provide a jade with lifelike effects, rich colors, luxurious appearance, solemn and elegant appearance, high transpare...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more