Acrylic ester high molecular type surfactant and preparation of porous resin
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An acrylate and surfactant technology, applied in the field of organic polymer compounds, can solve the problems of insufficient dispersion and emulsification of small molecule surfactants, and achieve the effect of sufficient emulsification and good performance
Inactive Publication Date: 2008-11-12
黄东东 +1
View PDF0 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The purpose of the present invention is to avoid the deficiencies in the prior art, overcome the shortcomings of insufficient dispersion and emulsification of traditional small molecule surfactants, provide a kind of acrylic ester random copolymerization polymer surfactant and its preparation method
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] Embodiment 1: Preparation of acrylate polymer surfactant.
[0031] Add 380mL of deionized water into the reaction flask, stir, protect with nitrogen, heat up to 67 degrees, add 56.4 grams of isobutyl methacrylate, 3.6 grams of methacryloyloxyethylammonium bromide (dimethylbutyl) , the initiator azobisisobutylamidine dihydrochloride 0.5 g, reacted for 12 hours, added acetone to terminate the reaction, lowered the temperature, washed with ether, and dried in vacuum to obtain a polymer acrylate surfactant.
Embodiment 2
[0032] Embodiment 2: Preparation of porous resin
[0033] Add 600 milliliters of cyclohexane into the reaction flask, 2.5 grams of acrylate polymer surfactant prepared in Example 1 above, 30 grams of water, heat to 50 degrees, stir, and after ultrasonic treatment for 24 hours, nitrogen protection, heat to 73 degrees, add:
[0034] Butyl methacrylate 0.3 g
[0035] Methacrylamide 3.5g
[0036] Allyl glycidyl ether 6.6g
[0037] Glycidyl methacrylate 6.8 g
[0038] Methylenebis(methacrylamide) 16.7g
[0039] Azobisisobutyronitrile 0.7 g
[0040] After reacting for 6 hours, filter, rinse with acetone, and dry in vacuum to obtain a porous resin.
Embodiment 3
[0041] Embodiment 3: Preparation of acrylate polymer surfactant.
[0042] Add 380mL of deionized water into the reaction flask, stir, protect with nitrogen, heat up to 73 degrees, add 56.4 grams of butyl methacrylate, 3.6 grams of sodium methacrylsulfonate, and 0.5 grams of initiator azobisisobutyronitrile After 12 hours of reaction, acetone was added to terminate the reaction, the temperature was lowered, washed with ether, and dried in vacuum to obtain a high molecular weight acrylate surfactant.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to acrylic macromolecular surfactant and a method for making the porous resin of the same, belonging to the organic macromolecular compound field. The acrylic macromolecular surfactant comprises 93 to 97 percent of acrylic substance, 3 to 7 percent of vinyl ion reagent and 0.5 to 1 percent of initiator. The substances are added in a reactor containing an amount of water, and are reacted at a temperature controlled between 57 and 80 DEG C for 6 to 24 hours; then, the reactants undergo acetone deposition, ether scrubbing and deposition and vacuum drying. The porous resin is made through adopting the following steps that: the acrylic macromolecular surfactant, monomer, initiator and a crosslinking agent are added in water, cyclohexane or the mixed solution of water and cyclohexane; and round porous resin is made by means of emulsion polymerization under the action of the initiator. The method makes the porous resin by means of the acrylic macromolecular surfactant, wherein the surfactant has excellent performances and full emulsification; and the porous resin is round in shape with the diameter ranging between 50 and 500 micron. The porous resin made by the method contains active epoxy group, and can be used in the fields of enzyme immobilization, antibody adsorption and purification and blood pathogen or toxin cleaning, etc.
Description
technical field [0001] The preparation method of the acrylate polymer surfactant and the porous resin of the present invention belongs to the field of organic polymer compounds. Background technique [0002] With the in-depth research in the fields of environmentally friendly water-soluble coatings, enhanced oil recovery, drug carriers, biomimicry, medical polymer materials, and emulsion suspension polymerization, higher requirements are placed on the diversity and performance of surfactants, among which polymer surface Activity is increasingly becoming the focus of attention. Compared with low-molecular surfactants, high-molecular surfactants have a higher molecular weight and can form unimolecular micelles or multi-molecular micelles. The solution has high viscosity and good film-forming properties, and has good dispersion, emulsification, thickening, Stability and flocculation performance. At present, polymer surfactants are widely used in many important basic industrie...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more