Ultra high temperature lubricating grease and production method thereof

A kind of grease, ultra-high temperature technology, applied in the direction of lubricating composition, petroleum industry, additives, etc., can solve the problems of smoke, easy dripping, loss, etc., to prevent sintering, prolong service life, good high temperature resistance. Effect

Active Publication Date: 2012-01-11
无锡中石油润滑脂有限责任公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During use, it is easy to drip oil, lose oil, coke and carbon deposit at high temperature, which will cause bearing damage; smoke will be emitted during use, which will have an impact on the human body and the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra high temperature lubricating grease and production method thereof
  • Ultra high temperature lubricating grease and production method thereof
  • Ultra high temperature lubricating grease and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment one: the production method of a kind of ultra-high temperature lubricating grease of the present invention adopts the following process steps: its component ratio is counted by weight parts:

[0022] Take synthetic ester oil: 50 parts, lipophilic silica powder: 10 parts, eutectic rolling ball: 1 part, colloidal graphite: 30 parts, copper powder: 7.9 parts, boron nitride: 1 part , Dialkyl diphenylamine is 0.1 part, and the above formula is a component of the ultra-high temperature lubricating grease of the embodiment of the present invention.

[0023] Add synthetic ester oil and silicon dioxide powder into the open reaction kettle, start stirring after adding, stirring speed: 30 rpm; stirring time: 30 minutes; heat up to 120°C; heat preservation reaction for 1 hour (stirring is not stopped); After the heat preservation is over, stop stirring, add eutectic rolling balls, colloidal graphite, copper powder, boron nitride, dialkyl diphenylamine, start stirring, st...

Embodiment 2

[0026] A production method of ultra-high temperature lubricating grease of the present invention adopts the following process steps: the component ratio is calculated in parts by weight:

[0027] Take synthetic ester oil: 65 parts, lipophilic silica powder: 14 parts, eutectic rolling ball: 2 parts, colloidal graphite: 14 parts, silver powder: 2.8 parts, boron nitride: 2 parts, Dialkyl diphenylamine is 0.2 parts, and the above formula is the ultra-high temperature lubricating grease component of the present invention.

[0028] Add synthetic ester oil and silicon dioxide powder into the open reaction kettle, start stirring after adding, stirring speed: 30 rpm; stirring time: 30 minutes; heat up to 100°C; heat preservation reaction for 1.5 hours (stirring is not stopped); After the heat preservation is over, stop stirring, add eutectic rolling balls, colloidal graphite, copper powder, boron nitride, dialkyl diphenylamine, start stirring, stirring speed: 20 rpm; stirring time: 30 ...

Embodiment 3

[0029] Embodiment three: the production method of a kind of ultra-high temperature lubricating grease of the present invention adopts following process steps: its component ratio is counted by weight parts:

[0030] Take synthetic ester oil: 80 parts, lipophilic silica powder: 16 parts, eutectic rolling ball: 1 part, colloidal graphite: 1 part, gold powder: 0.7 parts, boron nitride: 1 part, 0.3 part of dialkyl diphenylamine is the ultra-high temperature lubricating grease component of the present invention.

[0031] Add synthetic ester oil and silicon dioxide powder into the open reaction kettle, start stirring after adding, stirring speed: 30 rpm; stirring time: 30 minutes; heat up to 150°C; heat preservation reaction for 2 hours (stirring is not stopped); After the heat preservation is over, stop stirring, add eutectic rolling balls, colloidal graphite, copper powder, boron nitride, dialkyl diphenylamine, start stirring, stirring speed: 20 rpm; stirring time: 30 minutes; aft...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to ultra-high temperature lubricating grease and a production method thereof, which belongs to the technical field of lubricant in the chemical industry. The production method comprises the following steps: adding synthetic ester oil and silicon dioxide powder to a reaction vessel for stirring, temperature rising, reacting, and heat insulating; adding an anti-wear agent, aquadag, metal powder, boron nitride and antioxidant, and then fully stirring and refluxing; and filtering, grinding, and obtaining the finished product. Because silicon dioxide inorganic thickener is adopted to thicken the ester oil, the ester oil is used as the basic lubricating grease which has good high-temperature resistance, without oil dripping, draining, coking and carbon accumulation at hightemperature, and various high temperature additives including graphite, metal powder and boron nitride are added, lubrication under the ultra-high temperature condition can be ensured, and bearing sintering can be prevented; lubrication in special positions and high temperature positions can be achieved, and the service life of equipment can be prolonged.

Description

technical field [0001] The invention relates to an ultra-high temperature lubricating grease and a production method, belonging to the technical field of lubricating materials in the chemical industry. Background technique [0002] In the prior art, ultra-high temperature lubricating grease is usually made by mixing 10-25 parts of lithium-based thickener, 40-60 parts of thickened mineral oil, and 20-60 parts of some solid lubricants such as graphite. This kind of lubricating grease is usually used at a high temperature of 600°C-800°C for the lubrication of high-temperature parts of equipment in steelmaking, printing and dyeing, papermaking and other industries. During use, it is easy to drip oil, lose oil, coke and carbon deposits at high temperatures, resulting in bearing damage; smoke will be emitted during use, which will have an impact on the human body and the environment. Contents of the invention [0003] The purpose of the present invention is to overcome the abov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M125/20C10N30/06
Inventor 张江杨晓钧
Owner 无锡中石油润滑脂有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap