Continuous casting mould fluxes and preparation method thereof

A technology of continuous casting mold flux and mold flux, which is applied in the field of continuous casting mold flux and its preparation, can solve the problems of low delamination defect rate, inability to reduce delamination defect rate, and poor effect, and achieve low delamination defect rate, Effects of improving operational safety and reducing longitudinal and subcutaneous cracks

Inactive Publication Date: 2011-08-31
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the poor effect of the existing continuous casting mold powder on reducing the longitudinal cracks on the surface of the slab, and it cannot reduce the transverse cracks and subcutaneous network cracks on the surface of the slab, resulting in a finished steel product after the slab is rolled. It provides a continuous casting protection that can effectively reduce the longitudinal cracks, transverse cracks and subcutaneous network cracks on the surface of the slab, so that the finished steel product after the slab is rolled has a low rate of delamination defects. slag

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0018] The preparation method of the continuous casting mold flux provided by the present invention includes uniformly mixing calcium-containing compounds, silicon-containing compounds and aluminum-containing compounds, wherein the method also includes adding additives, and the additives are selected from making the melting point and melting point of the mold flux One or more of the compounds with reduced viscosity in the state, the amount of the additive reduces the melting point of the mold flux to 1070-1170°C, and the viscosity at 1300°C to 0.2-0.4Pa·S; and In terms of weight, the weight ratio of the calcium-containing compound to the silicon-containing compound in the mold flux is 0.95-1.15, and the weight ratio of the aluminum-containing compound to the calcium-containing compound is 0.15-0.5.

[0019] According to the preparation method of the continuous casting mold flux provided by the present invention, the various components forming the continuous casting mold flux ca...

Embodiment 1

[0023] This example is used to illustrate the continuous casting mold flux provided by the present invention and its preparation method.

[0024] 30 kg of wollastonite, 6 kg of quartz sand, 15 kg of bauxite, 22 kg of Na 2 CO 3 , 14 kg of magnesia, 12 kg of fluorite (these raw materials are equivalent to 25 kg of CaO, 25 kg of SiO 2 , 12.5 kg of Al 2 o 3 , 12.5 kg of Na 2 O, 14 kg of MgO, 6 kg of F - ), 1 kg Fe 2 o 3 After mixing with 2 kg of MnO, it is melted in an electric furnace to prepare a premelt with a particle diameter of 5-60 microns. Then this premelt is mixed with 1 kilogram of semi-reinforcing carbon black and 1 kilogram of super carbon black, then mix evenly with a stirrer, then mix 400 kilograms of water and make the mixture a slurry with a concentration of 20% by weight through a ball mill, Finally, under the conditions of a pressure of 2 MPa, an inlet air temperature of 800°C, an exhaust gas temperature of 200°C, and a nozzle diameter of 2 mm, the slurr...

Embodiment 2

[0031] This example is used to illustrate the continuous casting mold flux provided by the present invention and its preparation method.

[0032] 22 kg of wollastonite, 15 kg of limestone, 18 kg of cement clinker, 14 kg of quartz sand, 10 kg of bauxite, 9 kg of Na 2 CO 3 , 5 kg of magnesia, 6 kg of fluorite (these raw materials are equivalent to 39 kg of CaO, 34 kg of SiO2, 10 kg of Al 2 o 3 , 5 kg of Na 2 O, 5 kg of MgO, 3 kg of F - ) and 1 kg of Fe 2 o 3 After mixing, melt it with an electric furnace to form a premelt with a particle diameter of 5-60 microns, then mix the premelt with 1.25 kg of semi-reinforcing carbon black and 1.75 kg of Zhongchao carbon black, and then mix it with a mixer Uniformly, then mix 25 kg of water through a ball mill to make the mixture into a slurry with a concentration of 80% by weight. Finally, the pressure is 2 MPa, the air inlet temperature is 800 ° C, the exhaust gas temperature is 200 ° C, and the diameter of the spray sheet is 2 mm....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides continuous casting protection slag, which contains a calcium-contained compound, a silicon-contained compound and an aluminum-contained compound, wherein the protection slag also contains an addictive; the addictive selects from one or more of compounds which make the melting point and the viscocity in the melting state of the protection slag reduced; the dosage of the addictive makes the melting point of the protection slag reduced to be between 1,070 and 1,170 DEG C, and the viscocity of the protection slag at the temperature of 1,300 DEG C reduced to be between 0.2 and 0.4 Pa.S; and based on oxide, the weight ratio of the calcium-contained compound to the silicon-contained compound of the protection slag is between 0.95 and 1.15, and the weight ratio of the aluminum-contained compound to the silicon-contained compound is between 0.15 and 0.5. Compared with the prior continuous casting protection slag, the continuous casting protection slag provided by the invention can effectively reduce longitudinal cracks, transverse cracks and subsurface meshy cracks on the surface of casting banks, and the splitting defect rate of steel finished products subjected to casting blank rolling is lower.

Description

technical field [0001] The invention relates to a continuous casting mold flux and a preparation method thereof. Background technique [0002] The content of Cu, Cr, Ni, Al, V, N elements in the composition of vanadium-containing high-nitrogen steel is relatively high, and the carbon content is also just in the peritectic reaction zone. The unique composition determines the casting difficulty of this steel type , such as [C], [Cu], [Cr], [Ni], [Al], [V] and [N] in the steel have a great influence on the surface quality and subcutaneous quality of the slab, especially those containing vanadium, aluminum and high nitrogen Steel, [Al], [V] in solid solution at high temperature will be dynamically precipitated or statically precipitated in the form of AlN, V(CN) at the austenite grain boundary when the temperature decreases, increasing the source of stress concentration and crack sensitivity, arc When the caster slab is straightened, the inner arc is subjected to tensile stress...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/111
Inventor 曾建华吴国荣陈永周伟杨素波张均祥李茂林杨秀亮唐生斌
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap