Aluminum zirconium middle alloy and preparation method thereof

A master alloy, aluminum zirconium technology, applied in the field of aluminum zirconium master alloy and its preparation, can solve the problems of long production and processing cycle, high processing cost, complex process, etc. Effect

Inactive Publication Date: 2009-10-07
毕祥玉
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, my country's aluminum zirconium (AlZr 4 ) The master alloy is completed by melting and remelting aluminum ingots. Due to the complex process and long production and processing cycle, the processing cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1. Raw material ratio:

[0022] (1) Analyze the composition of various materials and the composition of the original aluminum liquid. The zirconium content of the sponge zirconium powder is 99%, the silicon content in the original aluminum liquid is 0.1%, the iron content is 0.12%, and the aluminum content is 99.97%.

[0023] (2) Calculate the amount of various materials added according to the zirconium content required by the national standard (calculated in a 10T furnace). Considering the burning loss and local segregation, the amount of various alloys should be added according to the calculation theory of the upper line of the GB8735-88 national standard quantity.

[0024] (3) Input amount of alloy and raw aluminum liquid (calculated on a 10T furnace): 8T of raw aluminum liquid, 0.5T of sponge zirconium powder, appropriate amount of refining agent and covering agent.

[0025] 2. Preparation method:

[0026] The method of directly using the original aluminum liquid ...

Embodiment 2

[0031] 1. Raw material ratio:

[0032] (1) Analyze the composition of various materials and the composition of the original aluminum liquid. The zirconium content of the sponge zirconium powder is 99.8%, the silicon content in the original aluminum liquid is 0.01%, the iron content is 0.01%, and the aluminum content is 99.99%.

[0033] (2) Calculate the amount of various materials added according to the zirconium content required by the national standard (calculated in a 10T furnace). Considering the burning loss and local segregation, the amount of various alloys should be added according to the calculation theory of the upper line of the GB8735-88 national standard quantity.

[0034] (3) Input amount of alloy and raw aluminum liquid (calculated on a 10T furnace): 9T of raw aluminum liquid, 0.39T of sponge zirconium powder, appropriate amount of refining agent and covering agent.

[0035] 2. Preparation method

[0036] The method of directly using the original aluminum liqu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aluminum zirconium middle alloy and a preparation method thereof; the aluminum zirconium middle alloy is made from main materials and auxiliary materials; the main materials are primary aluminum liquid and sponge zirconium powder; the auxiliary materials are refining agent and covering agent. The invention is characterized in that the alloy comprises the following components by weight: 99 percent to 99.9 percent of zirconium in the sponge zirconium powder; 0.01 percent to 0.1 percent of silicon, 0.01 percent to 0.12 percent of iron and 99.97 percent to 99.99 percent of aluminum in the primary aluminum liquid. The using amount of the alloy and the primary aluminum liquid (calculated according to a 10T furnace) is as follows: 8T to 9T of primary aluminum liquid, 0.39T to 0.5T of sponge zirconium powder, and appropriate amount of refining agent and covering agent. The invention has the advantage of achieving the purpose of energy conservation and environmental protection by using the method of producing aluminum zirconium middle alloy by the primary aluminum liquid, thereby greatly lowering the investment cost, shortening the production period, simplifying the production process, and reducing the processing cost.

Description

technical field [0001] The invention relates to an aluminum-zirconium master alloy and a preparation method thereof, belonging to the technical field of nonferrous metals. Background technique [0002] At present, my country's aluminum zirconium (AlZr 4 ) The master alloy is completed by melting and remelting aluminum ingots. Due to the complex process and long production and processing cycle, the processing cost is relatively high. In order to reduce energy consumption, reduce investment and shorten production cycle. We used the original aluminum liquid to try to produce aluminum-zirconium master alloy. After more than half a year of hard work, good results have been achieved, and an aluminum-zirconium-aluminum-zirconium master alloy has emerged as the times require. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prior art and provide an aluminum-zirconium master alloy and its preparation method. The alumi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/00C22C16/00
Inventor 毕祥玉
Owner 毕祥玉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products