Novel stitch knitting stitch bond fabric and preparation method thereofd

A manufacturing method, the technology of Lixin cloth, which is applied in the fields of seam trimming, non-woven fabrics, textiles and papermaking, etc., can solve the problems of uneven fiber thickness, uneven carding and fragile fibers, etc., and achieve air permeability Good, good antibacterial performance, strong moisture absorption effect

Inactive Publication Date: 2009-11-11
福建鑫华股份有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are many problems in raw bamboo fiber, such as: uneven fiber thickness, small or no curl, brittle fiber, uneven carding, and it is necessary to retain its excellent antibacterial properties in the sewing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example one:

[0020] The new type of stitch-woven celestial fabric of the present invention is made of 30wt% bamboo raw fibers with a fiber fineness of 1-7D and a fiber length of 25-70mm and 70wt% of chemical fibers through a non-woven method. Among them, the chemical fiber used is polyester fiber, polypropylene fiber or acrylic fiber.

[0021] The method for manufacturing a new type of stitch-bonded celestial fabric of the present invention uses a mixture of bamboo raw fibers with a fiber fineness of 1-7D and a fiber length of 25-70mm and 70% by weight of chemical fibers as raw materials. It is manufactured by opening, carding, netting, stitching and stenter setting processes in sequence. Among them, the chemical fiber used is polyester fiber, polypropylene fiber or acrylic fiber. among them:

[0022] The opening process is: the raw bamboo fiber and chemical fiber are fed into the opening machine to maximize the fluffy state and mix them evenly;

[0023] The carding proce...

Example Embodiment

[0027] Embodiment two:

[0028] The difference between the second embodiment and the first embodiment of a new type of stitch-woven celestial heart cloth of the present invention is that the raw bamboo fiber is 90% by weight, and the chemical fiber is 10% by weight.

[0029] In the method for manufacturing a new type of stitch-woven celestial fabric of the present invention, the difference between the second embodiment and the first embodiment is only that: the raw bamboo fiber is 90% by weight, and the chemical fiber is 10% by weight.

Example Embodiment

[0030] Embodiment three:

[0031] The difference between the third embodiment and the first embodiment of a new type of stitch-woven fabric of the present invention is that the raw bamboo fiber is 60% by weight, and the chemical fiber is 40% by weight.

[0032] In the method for manufacturing a new type of stitch-bonded celestial fabric of the present invention, the difference between the second embodiment and the first embodiment is only that: the raw bamboo fiber is 60% by weight, and the chemical fiber is 40% by weight.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel stitch knitting stitch bond fabric and a preparation method thereof. The stitch bond fabric is prepared by raw material of mixed material of 30-100wt% of raw bamboo fiber with the fiber fineness of 1-7D and the fiber length of 25-70mm and 0-70wt% of chemical fiber through opening, carding, lapping, stitch knitting and tentering sizing procedures in sequence. The invention takes natural degradable raw bamboo fiber as main raw material and has the advantages of environment protection and degradable ability, good antibacterial action and strong hydroscopic property and the like, wherein the bacteriostasis rate reaches 60-90%, and the moisture regain of 120min at 140 DEG C is more than or equal to 8; besides, fiber web is only processed by stitch hemming for reinforcement, the undisturbedness of the fiber web is maintained, poriness is high, and ventilation property is excellent, the ventilation property of 120min at 140 DEG C is more than or equal to 200L/dmmin. Meanwhile, the product has small thermal contractibility through the tendering sizing procedure, and the thermal contractibility of 120min at 140 DEG C is less than or equal to 1%.

Description

technical field [0001] The invention relates to the application field of stitch-bonding of nonwoven fabrics, in particular to a stitch-bonded Lixin cloth and a manufacturing method thereof. Background technique [0002] At present, Lixin cloth produced by stitching technology in the field of non-woven fabrics is mainly made of non-degradable chemical fibers. For example, polyester fiber, polypropylene fiber, acrylic fiber, etc. are used as raw materials. These fibers are thermoplastic fibers. The Lixin cloth produced is relatively poor in air permeability and moisture absorption performance, and has no natural antibacterial effect. [0003] Bamboo fiber has the advantages of excellent antibacterial, good air permeability, and strong hygroscopicity, which have been widely recognized by everyone. At present, bamboo pulp fibers made of bamboo as raw materials have been applied to various fields of textiles, but due to previous production costs and technical conditions Factors ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/70D06C13/12D06C7/02D04H1/4382
Inventor 郭秉臣黄清保杨道光粘伟诚洪明取
Owner 福建鑫华股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap