Method for cast-rolling blank for producing deep-drawing daily aluminum product
An aluminum product, cast-rolling technology, applied in the field of deep-drawing daily-use aluminum product blanks, can solve the problems of poor deep-drawing performance, high production cost, complex production process, etc., achieve uniform product thickness, increase production efficiency, and produce The effect of simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] The present invention takes 1050 deep-drawing aluminum as an example, and adopts the following process to produce (the following is the same as embodiment one):
[0024] 1), smelting casting and rolling
[0025] (1), conventionally produced cast-rolled 1050 deep-drawn aluminum material is furnace-melted according to a conventional method;
[0026] (2) When all the aluminum materials are melted into molten aluminum, mix HSGJ-6 sodium-free refining agent and HT-LWQ sodium-free slag powder 0.5 hours before turning down the furnace, and mix them with nitrogen Spray into molten aluminum with a spray pressure of 20MPa;
[0027] The added nitrogen is high-purity nitrogen with a purity of 99.999%;
[0028] During the process of melting the aluminum material, stir 4 times successively. The amount of sodium-free refining agent added is 0.12% of the weight of the aluminum melt, the amount of sodium-free slagging agent added is 0.08% of the weight of the aluminum material; the a...
Embodiment 2
[0036] The present invention adopts following process method to produce:
[0037] 1), smelting casting and rolling
[0038] (1), conventionally produced cast-rolled 1050 deep-drawn aluminum material is furnace-melted according to a conventional method;
[0039] (2) When all the aluminum materials are melted into molten aluminum, mix the HSGJ-6 sodium-free refining agent and HT-LWQ sodium-free slag agent powder 0.5 hours before turning down the furnace, and use 20MPa together with nitrogen The injection pressure is sprayed into the molten aluminum; the added nitrogen is high-purity nitrogen with a purity of 99.999%;
[0040] Stir 5 times successively during the process of melting the aluminum material. The amount of sodium-free refining agent added is 0.1% of the weight of aluminum melt, the amount of sodium-free slagging agent added is 0.1% of the weight of the aluminum material, and the amount of nitrogen added is 0.85% of the weight of the aluminum material; The sodium-fr...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap