Lithium ion battery packaging film and manufacturing method thereof

A technology of lithium-ion batteries and manufacturing methods, which is applied to battery pack parts, chemical instruments and methods, circuits, etc., can solve the problems of high cost, poor compactness, and short life of lithium-ion battery packaging films, and achieve less pores and higher density Good sex and long life effect

Active Publication Date: 2013-04-03
沈道富
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention requires a flexible laminated film and a rigid laminated film to form a lithium-ion battery laminated film (equivalent to a lithium-ion battery packaging film), and each layer of the flexible laminated film and the rigid laminated film needs to be bonded by an adhesive layer Together, the resulting lithium-ion battery packaging film is expensive, and each adhesive layer is easily delaminated and dense under the corrosion of the electrolyte (mainly composed of carbonates and lithium hexafluorophosphate) and HF (hydrofluoric acid). Poor performance, many pores, short service life, the service life is generally two years

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ion battery packaging film and manufacturing method thereof
  • Lithium ion battery packaging film and manufacturing method thereof
  • Lithium ion battery packaging film and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Such as figure 1 As shown, the lithium-ion battery packaging film of the first invention of the present application has a laminated laminated structure. The surface layer 1 is various types of nylon with a thickness of 0.01-0.1mm. The various types of nylon refer to nylon 6 engineering plastics, nylon 66 engineering plastics, nylon 610 engineering plastics, nylon 1010 engineering plastics, alcohol-soluble nylon, three Copolycondensation nylon (insoluble), reinforced nylon 66 engineering plastics, etc. The inner layer 2 is various types of aluminum foils with a thickness of 0.01-0.1 mm. The surface layer 3 is various types of CPP (polypropylene), the thickness of which is 0.01-0.1mm. The various types of CPP are PP, CPP or fluorinated polypropylene and other types of PP or modified PP. The lithium-ion battery packaging film does not have an adhesive layer, that is, it does not contain various hot-melt adhesives, that is to say, there is no substance corroded by the lit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a lithium ion battery packaging film which has a layered pressing structure, and a manufacturing method thereof comprises the following steps: fetching an aluminum foil after chemical hydrofluoric acid control processing, wherein the thickness of the aluminum foil is 0.01-1.0mm; fetching a nylon film with the thickness of 0.01-0.1mm; fetching a CPP (polypropylene) film with the thickness of 0.01-0.1mm; and overlaying the CPP film, the aluminum foil and the nylon film together and hot-pressing. The lithium ion battery packaging film has no bonding layer, namely, does not contain various hot melt adhesives, in other words, has no matters that are corroded by lithium ion battery electrolytes and hydrofluoric acid, thereby the lithium ion battery packaging film can not be layered, and has good compactness, less pore spaces, long service life and more than 20 years of life span. The lithium ion battery packaging film is formed by directly and physically pressing, and various hot melt adhesives are unnecessary to be coated among the layers, namely, the hot melt adhesives are saved; the invention has short manufacturing process and low material cost; and meanwhile, the product is suitable for manufacturing large-capacity batteries.

Description

technical field [0001] The invention relates to a lithium ion battery packaging film and a manufacturing method thereof, in particular to a special packaging film for soft packaging lithium ion batteries and polymer lithium ion batteries and a manufacturing method thereof. Background technique [0002] An invention patent application with a document number of CN101197431A discloses a laminated film covering battery elements for a lithium-ion battery pack. The laminated film structure is an outer packaging layer / metal layer / sealant layer, such as Ny / Al / CPP, The three layers are bonded together through the adhesive layer; according to the material type of the middle metal layer, it can be divided into flexible laminated film and rigid laminated film, and the flexible laminated film and rigid laminated film are bonded through the thermal adhesive layer. Together; the thermal adhesive layer is formed by coating hot melt resins such as ethylene vinyl alcohol resin and ethylene-vi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/02B32B27/08B32B15/08B32B15/20B32B37/06B32B37/12H01M50/129
CPCY02E60/12Y02E60/10
Inventor 沈道付
Owner 沈道富
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com