Environmental functional material applied to electroplating wastewater treatment
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for functional materials and electroplating wastewater, applied in the fields of metallurgical wastewater treatment, water/sewage treatment, adsorbed water/sewage treatment, etc., can solve the problems of restricting the popularization and use of recapture agents, high treatment costs, and achieving difficulty in secondary pollution, Simple equipment and convenient operation
Inactive Publication Date: 2010-02-17
NANJING NORMAL UNIVERSITY
View PDF0 Cites 17 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the processing cost is high, which limits the promotion and use of recapture agents
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] Add 20% modified diatomaceous earth, 40% humic acid and 40% chitosan into the mixer according to the above ratio, and mix for 2 hours to obtain a multifunctional environment-friendly material that can be applied to electroplating wastewater treatment.
Embodiment 2
[0018] 30% attapulgite, 10% kaolin, 40% humic acid and 20% chitosan were added into the mixer according to the above proportions, and mixed for 3 hours to obtain a multifunctional environment-friendly material that can be applied to electroplating wastewater treatment.
Embodiment 3
[0020] 50% modified diatomite, 5% bentonite, 5% attapulgite, 30% humic acid and 10% chitosan were added to the mixer according to the above ratio and mixed for 4 hours to obtain Multifunctional environment-friendly material for handling.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an environmental functional material applied to electroplating wastewater treatment; all components are as follows by mass percentage; kieselguhr, modified purified diatomite,bentonite, modified purified bentonite, attapulgite, modified purified attapulgite, kaoline and / or 20-80 percent of modified purified kaoline, 10-40 percent of humic acid and 10-40 percent of chitosan. The material has convenient usage, good treatment effect, and large and dense formed floccules, shortens settling time, and is easy to lead heavy metal ions, COD, ammonia-N, phosphorus, chromaticity and other indexes in wastewater to synchronously achieve discharge standard regulated nationally, the produced residue can recycle heavy metal, and secondary pollution is not easy to generate. Thematerial is suitable for treating wastewater in industries such as circuit boards, electro-plating, metal finishing, photographic film manufacturing, coal plants, municipal or industry waste incineration, battery production and the like.
Description
technical field [0001] The invention relates to a technology for removing, purifying or trapping heavy metal ions in water, in particular to a multifunctional environment-friendly material applied to the treatment of electroplating wastewater. Background technique [0002] Industries often produce wastewater containing chromium, nickel, copper, cadmium, lead, zinc, aluminum, gold, silver, mercury and other metal ions. Concentration and long-term toxic side effects and other characteristics, if not properly handled, will cause serious pollution to the environment. [0003] The traditional pH adjustment precipitation method treats wastewater containing heavy metal ions, that is, by adding alkaline chemicals such as sodium hydroxide, sodium carbonate, and lime, the pH value of the wastewater is adjusted to about 11, and the corresponding heavy metal hydroxide precipitates are formed. Remove heavy metal ions. For the pH adjustment precipitation method, the pH value needs to be...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.