Fluoridated dental composite resin material contributing to resisting secondary caries

A composite resin, secondary technology, used in dentistry, dental preparations, dental prostheses, etc., can solve the problems of unstable fluorine release of inorganic fluoride salts, reduction of overall toughness and wear resistance of composite resins, and achieve stable Release, good compatibility effect

Inactive Publication Date: 2012-07-25
江门市焯越义齿有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem to be solved by the present invention is to solve the problem of unstable release of fluorine from inorganic fluorine salts in the existing fluorine-doped composite resins for caries filling, and the impact on the composite resin caused by the naked doping of inorganic fluorine salts. In order to solve the problem of reducing the overall strength, toughness and wear resistance, a new fluorine-doped composite resin material for caries filling is developed to help prevent secondary caries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Weigh 10.00 grams of fluorine-loaded mesoporous silica microspheres, and 50.00 grams of barium strontium boron glass powder, and 40.00 grams of borosilicate glass powder, and mix the above three components uniformly by mechanical stirring to prepare a total The nano-inorganic powder that weighs 100.00 grams and contains multiple components is for subsequent use.

[0029] 2.50 grams of medical-grade silane coupling agent KH-570 were hydrolyzed under the action of acetic acid, and 40 milliliters of hydroalcoholic solution was added. The pre-mixed nano-inorganic powder containing multiple components is dispersed in ultrasonic waves, and then reacted at 50°C for 24 hours, moved to an oven, and dried at 80°C for 10 hours, then, use the water alcohol The solution was washed, then dried at 100° C. for 10 hours, dried, and pulverized to make modified nano-inorganic powders for future use, and the reserve amount was slightly greater than the required amount.

[0030] Add 5.00 g...

Embodiment 2

[0032] Weigh 80.00 grams of fluorine-loaded mesoporous silica microspheres, 15.00 grams of barium strontium boron glass powder, and 5.00 grams of nano-hydroxyapatite, and uniformly mix the above three components by mechanical stirring to prepare The nanometer inorganic powder that total weight is 100.00 grams contains multiple components, standby.

[0033] 2.00 grams of medical grade silane coupling agent KH-570 was hydrolyzed under the action of acetic acid, and 400 milliliters of hydroalcoholic solution was added. The premixed nano-inorganic powder containing multiple components is dispersed in ultrasonic waves, then reacted at 100°C for 2 hours, moved to an oven, and dried at 80°C for 2 hours, then, use the water alcohol The solution is washed, then dried at 80°C for 2 hours, and then heated to 100°C for 5 hours. After drying, it is pulverized to make a modified nano-inorganic powder, which is used for future use. The reserve amount is slightly larger than the required amou...

Embodiment 3

[0036] Weigh 45.00 grams of fluorine-loaded mesoporous silica microspheres, and 25.00 grams of barium-strontium-boron glass powder, and 10.00 grams of nano-hydroxyapatite, and 5.00 grams of strontium glass powder, and 5.00 grams of boron-aluminum glass powder , and, 10.00 grams of commercially available barium-aluminum glass powder were uniformly mixed with the above various components by means of mechanical stirring to prepare a nano-inorganic powder with a total weight of 100.00 grams containing multiple components, and set aside.

[0037] 10.00 grams of medical grade silane coupling agent KH-570 was hydrolyzed under the action of acetic acid, and 200 milliliters of hydroalcoholic solution was added. The premixed nano-inorganic powder containing multiple components is dispersed in ultrasonic waves, then reacted at 100°C for 2 hours, moved to an oven, and dried at 80°C for 2 hours, then, use the water alcohol The solution was washed, then dried at 80°C for 12 hours, and then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a fluoridated dental composite resin material contributing to resisting secondary caries, and belongs to the field of dental preparations. The conventional simple villiaumite-blended composite resin caries-filling material has the problems of too quick fluorine release, poor interfacial compatibility and no rigid support for a caries-filling body, and the scheme aims to solve the problems. The fluoridated dental composite resin material comprises the following components in percentage by weight: 20 to 85 percent of nano inorganic powder of which the surface is modified by a silane coupling agent, 8 to 70 percent of bisphenol A glycidyl methacrylate resin monomer, 5 to 25 percent of triethylene-glycol dimethacrylate diluent, 0.25 to 2 percent of camphorquinone photoinitiator, and 0.5 to 3 percent of dimethylamino ethyl methacrylate coinitiator; and importantly, the nano inorganic powder comprises 10 to 80 weight percent of fluorine-carrying mesoporous silica microspheres which can slowly release fluorine and strengthen the composite resin.

Description

technical field [0001] The invention relates to a fluorine-containing dental composite resin material which is helpful for resisting secondary caries, and belongs to the field of A61K medical and dental preparations. Background technique [0002] In view of its comprehensive advantages, composite resin is a caries filling material that is gradually popular in clinical practice. [0003] Composite resins for caries filling can be roughly divided into two categories: single-paste composite resins and double-paste composite resins. Accompanied by a certain volume shrinkage, no matter what kind of composite resin is used for caries filling, micro-cracks are likely to occur on the edge of caries-filled fillings, which will cause edge micro-leakage and cause secondary caries. [0004] Many studies have shown that if the cavity filling material has the ability to release fluoride ions, the secondary caries at the edge of the cavity filling will be significantly reduced, because th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K6/083A61K6/027A61P1/02
Inventor 李榕生李榕卿
Owner 江门市焯越义齿有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com