Elastic putty and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An elastic putty and slaked lime technology, applied in the direction of filling slurry, etc., can solve the problems of peeling, coating peeling, affecting the use function and appearance of buildings, etc., to achieve the effect of reducing impact, good bonding strength and moderate price
Active Publication Date: 2011-06-15
上海基成达申防水材料有限公司
View PDF0 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Tortoise cracks cause water seepage on the back surface of the coating, which leads to peeling and peeling of the coating, and even affects the function and appearance of the building
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] (1) 25 kg of cement, 10 kg of steel slag, 2 kg of slaked lime, 40 kg of calcium carbonate, 20 kg of quartz sand (100 mesh), 1 kg of cellulose ether, 0.1 kg of lignocellulose, 0.01 kg of starch ether, powdered 0.4 kg of water repellent, 4 kg of dispersible rubber powder; all powders were added to the disperser, and stirred for 45 minutes at a speed of 1440rpm; elastic putty was obtained;
[0031] (2) Weigh the package.
Embodiment 2
[0033] (1) 20 kg of cement, 10 kg of fly ash, 3 kg of slaked lime, 30 kg of calcium carbonate, 25 kg of quartz sand (200 mesh), 0.4 kg of cellulose ether, 0.2 kg of lignocellulose, 0.04 kg of starch ether, 0.2 kg of powdery water repellent, 6 kg of dispersible rubber powder; add all the powder into the disperser, and stir for 45 minutes at a speed of 1440 rpm; make elastic putty;
[0034] (2) Weigh the package.
Embodiment 3
[0036] (1) 20 kg of cement, 15 kg of fly ash, 4 kg of slaked lime, 30 kg of calcium carbonate, 30 kg of quartz sand (150 mesh), 0.4 kg of cellulose ether, 0.2 kg of lignocellulose, 0.04 kg of starch ether, 0.1 kg of powdery water repellent, 10 kg of dispersible rubber powder; add all the powder into the disperser and stir for 45 minutes at a speed of 1440rpm; make elastic putty;
[0037] (2) Weigh the package.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
particle size
aaaaa
aaaaa
particle size
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to elastic putty and a preparation method thereof. The elastic putty is made from the following raw materials in parts by weight: 20-25 parts of cement, 10-15 parts of fly ash or steel slag, 2-6 parts of white lime, 30-40 parts of calcium carbonate, 20-30 parts of quartz sand, 0.1-1 part of cellulose ether, 0.1-0.5 part of lignocellulose, 0.01-0.04 part of starch ether, 0.1-0.4 part of powdery water repellent and 4-15 parts of dispersible gelatine powder. The preparation method comprises the steps of adding all raw materials in a dispersion machine in proportion, and stirring the raw materials for 45 min to obtain the elastic putty. The elastic putty has good bonding strength with various materials, and has higher compressive strength, bending strength, tensile strength, permeability resistance and waterproof performance; the putty has flexibility after curing, strong protection properties, easy construction and good durability, is easy to foundry mill at early period while having high intensity at later period, is innoxious, flavourless and non-inflammable, and belongs to recycled product of industrial waste residues.
Description
technical field [0001] The invention relates to a putty and a preparation method thereof, in particular to an elastic putty and a preparation method thereof, belonging to the technical field of building materials. Background technique [0002] On the interior and exterior walls that have been coated with architectural paint, it is often found that the surface of the wall is rough, uneven, cracked, peeled and peeled off. Tortoise cracks cause water seepage on the back surface of the coating, which causes the coating to peel and fall off, and even affect the function and appearance of the building. Contents of the invention [0003] The purpose of the present invention is to overcome the above-mentioned defects in the prior art, and provide an elastic putty with excellent performance and convenient construction and a preparation method thereof. [0004] In order to achieve the above object, the technical solution of the present invention provides a kind of elastic putty, it...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 