Silicate cement adhesive for high-voltage electrical appliance bushing

A cement adhesive and Portland cement technology, which is applied in the field of Portland cement adhesive for high-voltage electrical appliances, can solve the problems of poor fluidity of the cement adhesive, influence on the mechanical strength of the finished product, insufficient strength of the adhesive, and the like. The effect of glue packing, guaranteeing operational performance and electromechanical performance, and excellent comprehensive performance

Inactive Publication Date: 2010-09-29
DALIAN INSULATOR GRP CO LTD
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, there are the following problems in glue binding of large-scale porcelain sleeves: the fluidity of the cement adhesive is poor, which is not conducive to the glue binding of workers; the ear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: A Portland cement adhesive for high-voltage electrical appliance porcelain sleeves. The raw material composition of the adhesive includes Portland cement, silica sand, water, and a water reducing agent. It is characterized in that the cement adhesive components and their The weight contents are: 30%-45% of cement; 25%-50% of silica sand [2]; 1.0%-5.5% of water reducing agent; 0.1%-2.0% of early strength agent; the balance is water.

Embodiment 2

[0017] Embodiment 2: The preferred components of the present invention and their weight content proportions are respectively: 35% to 40% of cement; 30% to 45% of silica sand; 1.5% to 4.5% of water reducing agent; 0.5% to 0.5% of early strength agent 1.8%; the balance is water.

Embodiment 3

[0018] Embodiment 3: The best components and weight content ratios of the present invention are: cement 36%-39%; silica sand 35%-40%; water reducing agent 2.5%-3.5%; early strength agent 0.8%- 1.5%; balance water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to silicate cement adhesive for a high-voltage electrical appliance bushing. The adhesive is prepared by combining and proportioning the following raw materials in percentage by weight: 30-45 percent of silicate cement, 25-50 percent of silica sand, 1.0-5.5 percent of water reducing agent, 0.1-2.0 percent of early strength agent and the balance of water, wherein the water reducing agent is of high-efficiency and reaches the water reducing effect of 25-50 percent to satisfy the high-mobility requirement and the strength requirement of the silicate cement for a bushing, the compactness and the early strength of the cement are enhanced by the early strength agent, and the production efficiency is improved. The invention adopting a formula of the raw materials and the proportion has excellent process performance and reasonable mechanical performance and satisfies the binding condition and the use safety requirement of the bushing.

Description

technical field [0001] The invention relates to a Portland cement adhesive for high-voltage electric appliance porcelain bushings (hereinafter referred to as porcelain bushings). More specifically, the present invention relates to a Portland cement adhesive for porcelain sleeves with high water-reducing properties, high fluidity, high strength and other excellent properties. Background technique [0002] With the continuous development of my country's electric power construction, more and more large-scale porcelain sleeves, which play an important role in power transmission and transformation projects, are used, and the plastic packaging of porcelain sleeves is also more and more valued by people. [0003] Cement adhesive is an important part of electric porcelain products, and it plays a role in integrating porcelain parts and metal accessories into a whole. In the prior art, there are the following problems in glue binding of large-scale porcelain sleeves: the fluidity of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B14/06
Inventor 赵明彪黄行平刘翃
Owner DALIAN INSULATOR GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap