Polypropylene high-filled toughening masterbatch and preparation method thereof

The technology of polypropylene and toughening masterbatch is applied in the field of polypropylene high filling and toughening masterbatch and its manufacturing field, which can solve the problems of waste of resources and low grade, achieve less waste disposal and investment, good environmental protection, and improve related performance. Effect

Inactive Publication Date: 2010-09-29
葛立武
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no professional system for the research and development of powder activation modification technology in China, and there is no specialized production base and market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene high-filled toughening masterbatch and preparation method thereof
  • Polypropylene high-filled toughening masterbatch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The technical solution of the present invention will be further elaborated below through specific examples.

[0018] A kind of preparation method of polypropylene high-filling toughening masterbatch described in the present invention, comprises the following steps:

[0019] 1. After ordinary calcite is processed into superfine heavy calcium carbonate powder, it is activated and modified by a high-pressure air flow machine to obtain a superfine modified powder.

[0020] 2. Ingredients: 150 kg of superfine modified powder, 14-17 kg of polypropylene resin, 3.15-3.85 kg of PP wax, 2.25-2.75 kg of PE wax, 1.8-2.2 kg of monoglyceride, 1.8-2.2 kg of aluminate Kilograms and 4 to 8 kilograms of calcium stearate are used for batching.

[0021] 3. Mixing: The above materials are fully mixed at a high temperature of 140-180°C.

[0022] 4. Pelletizing: After the uniformly mixed material is cooled, put it into the extruder again, and the temperature is controlled between 180 ~ 240 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Bending strengthaaaaaaaaaa
Flexural modulusaaaaaaaaaa
Login to view more

Abstract

The invention relates to a polypropylene high-filled toughening masterbatch and a preparation method thereof, and the preparation method comprises the following steps: taking ultra-fine active heavy calcium carbonate as a base, adding calcium carbonate powder, polypropylene resin, auxiliaries and a dispersing agent, carrying out activation and modification by a high-pressure gas flow machine, mixing, and carrying out extrusion molding for preparing the polypropylene high-filled toughening masterbatch. The filled masterbatch not only has large filling amount, but also still keeps the original excellent performances of plastic after filling, and improves the toughness, the rigidity and the smoothness of a product.

Description

technical field [0001] The invention relates to a high-filling and toughening master batch of polypropylene and a manufacturing method thereof. Background technique [0002] At present, only a few countries such as the United States, Germany, Japan, and South Korea have the technology and equipment to produce high-performance powders, and have strong advantages. At present, my country's powder chemical industry has always relied on imports for its demand for high-quality non-metallic mineral products. At present, there is no professional system for the research and development of powder activation modification technology in China, and there is no specialized production base and market. Some domestic powder companies, their products are primary raw materials with low grades, resulting in a great waste of various resources. And can not change the current backward status quo. Contents of the invention [0003] The object of the present invention is to provide a polypropylen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/08C08K13/06C08K9/00C08K3/26C08K5/098
Inventor 葛立武
Owner 葛立武
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap