Method for enhancing corrosion resisting property of Ni-W-P plating layer by adopting heat treatment technology
A kind of corrosion resistance, ni-w-p technology, applied in the coating, liquid chemical plating, metal material coating process and other directions, can solve the problem of reducing the corrosion resistance of the coating, to reduce the probability of damage, corrosion resistance The effect of improving and prolonging the service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Example 1
[0026] (1) Preparation of chemical plating solution
[0027] The contents of each component in each liter of plating solution are: nickel sulfate 20g / L, sodium tungstate 60g / L, sodium hypophosphite 20g / L, sodium citrate 70g / L, lactic acid 5ml / L, ammonium sulfate 20g / L, Sodium dodecylbenzenesulfonate 5mg / L, add deionized water to prepare plating solution, adjust pH value to 9.0 with sodium hydroxide solution;
[0028] (2) heating the above-mentioned plating solution to 90°C;
[0029] (3) Put the carbon steel sample into an alkaline degreasing bath for chemical degreasing at a temperature of 70°C, take it out after 15 minutes, and rinse with deionized water;
[0030] (4) Put the degreasing sample into the plating solution, and keep the temperature of the plating solution constant at 90°C;
[0031] (5) After 3 hours of plating, take out the sample and rinse with water to obtain a ternary Ni-W-P alloy;
[0032] (6) Heat treatment
[0033] The Ni-W-P coating...
Example Embodiment
[0035] Example 2
[0036] Corrosion resistance test: The Ni-W-P coating obtained in Example 1, the Ni-P coating after heat treatment under the same conditions, the as-plated Ni-P and Ni-W-P coatings were subjected to electrochemical tests at room temperature and 5% sulfuric acid. The obtained self-corrosion current density of each coating layer is shown in Table 1 below (the smaller the self-corrosion current density, the better the corrosion resistance).
[0037] Table 1 Corrosion performance comparison table of different coatings in 5% sulfuric acid
[0038] sample
Example Embodiment
[0039] Example 3
[0040] Corrosion resistance test: The Ni-W-P coating obtained in Example 1 was heat-treated at 600°C according to the method in Example 1 (6), and the coating and the Ni-P coating after heat treatment under the same conditions were plated as Ni-W-P coating. -P, Ni-W-P coatings were electrochemically tested in room temperature and 5% sulfuric acid, and the test results are shown in Table 2 below:
[0041] Table 2 Corrosion performance comparison table of different coatings in 5% sulfuric acid
[0042] sample
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap