Steel-aluminum compound hot rolled steel with tensile strength of 310MPa and production method thereof

A technology of tensile strength and steel-aluminum compounding, applied in the field of hot-rolled steel for parts, can solve the problems of adding more alloy elements, high cost, and high production cost, and achieve the effects of ensuring stability, improving stiffness, and reducing product cost

Inactive Publication Date: 2011-11-16
武汉钢铁有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional low-carbon steel or ultra-low carbon steel for steel-aluminum composite mainly has problems such as high aluminum content and high oxygen content, which lead to low performance of steel-aluminum composite and affect the normal use of materials
[0003] In the prior art, there are precious metal nickel elements added, and there are also steel-aluminum alloy materials, but the steel base is made of high manganese or high copper content. The disadvantage is that the cost is high and the production process is relatively complicated.
[0004] The Japanese patent document with the patent number JP 2005161383 discloses an invention in which a board is double-sided composite, wherein one side of the board is steel-aluminum composite, and the other side is steel-aluminum-zinc composite, and the steel base also contains Zirconium or magnesium, nickel, its deficiency adds more alloying elements, and the production cost is higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel-aluminum compound hot rolled steel with tensile strength of 310MPa and production method thereof
  • Steel-aluminum compound hot rolled steel with tensile strength of 310MPa and production method thereof
  • Steel-aluminum compound hot rolled steel with tensile strength of 310MPa and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] Describe in detail below

[0026] The components and weight percentages according to the present invention are as follows: the components and weight percentages are as follows: C: 0.004-0.006%, Si: <0.015%, Mn: 0.25-0.35%, Al: 0.0021-0.0030%, P: ≤0.022% , S: <0.006%, O: ≤0.003%, and the rest are Fe and unavoidable impurities. as well as

[0027] production method:

[0028] 1) Desulfurization is carried out to molten iron, and the percentage by weight of controlling S is <0.006%;

[0029] 2) Refining outside the furnace, control: the weight percentage of C is 0.004-0.006%, and the weight percentage of Al is 0.0021-0.003%;

[0030] 3) Carry out continuous casting, in the continuous casting process, adopt the covering agent that the weight percent of C is 0.1%, and adopt argon protection pouring, the flow rate of its argon is controlled at 11-13NM 3 / Hour;

[0031] 4) Heating the continuous casting slab, the heating temperature is controlled at 1220-1238°C;

[0032] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to hot rolled steel for radiators of central air conditioners. The hot rolled steel comprises the following components by weight percentage: 0.004-0.006% of C, less than 0.015% of Si, 0.25-0.35% of Mn, 0.0021-0.0030% of Al, not more than 0.022% of P, less than 0.006% of S, not more than 0.003% of O and the balance of Fe and inevitable impurities. The steps are as follows: carrying out desulfurization on molten iron; refining outside a furnace; carrying out continuous casting, and adopting a covering agent with 0.1% of C and argon for protecting pouring; heating a continuous casting slab to 1220-1238 DEG C; controlling the final rolling temperature of hot rolling to be 890-908 DEG C; and coiling and controlling the temperature to be 630-649 DEG C. The hot rolled steelcan replace an aluminum alloy plate heat exchanger of the central air conditioner, the production cost is low, and the hot rolled steel can lead the rigidity of the heat exchanger to be high and ensure the stability of the shape and the size of the heat exchanger.

Description

technical field [0001] The invention relates to steel for heat exchangers, especially suitable for heat exchangers with ultra-low carbon, ultra-low aluminum, and ultra-low oxygen characteristics of central air-conditioning, such as heat exchangers with a tensile strength of 310 MPa and an elongation of more than 46%. With hot rolled steel. Background technique [0002] The traditional low-carbon steel or ultra-low carbon steel for steel-aluminum composite mainly has problems such as high aluminum content and high oxygen content, which lead to low performance of steel-aluminum composite and affect the normal use of materials. [0003] In the prior art, there are precious metal nickel elements added, and steel-aluminum alloy materials are also available, but the steel base is selected with high manganese or high copper content. The disadvantage is that the cost is high and the production process is relatively complicated. [0004] The Japanese patent document with the patent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/06
Inventor 陈宇叶仲超李书瑞王立辉刘永前张彦文黄成红杨海林杜明
Owner 武汉钢铁有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More