Aerated concrete block and preparation method thereof

A technology of aerated concrete and blocks, which is applied in the manufacture of tools, ceramic products, and other household appliances, etc. It can solve the problems of poor sound insulation effect and heavy block weight, and achieve good thermal insulation performance, increase masonry speed, and good thermal insulation The effect of thermal insulation performance

Inactive Publication Date: 2010-12-15
舟山市宇锦新型墙体材料有限公司
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But it also has the above disadvantages: that is, the weight of the block is relatively large and the sound insulation effect is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] In the first embodiment, the basic composition of the aerated concrete block of the embodiment is as follows:

[0026] It is made of 250kg cement, 350kg lime, 1400kg silica sand, 1.45kg aluminum powder, 0.195kg foam stabilizer and water. The foam stabilizer is rosin or bone glue.

[0027] The preparation method of the aerated concrete block according to the above formula includes the following steps in sequence:

[0028] a. Preparation of raw materials: first mix cement and lime uniformly, then mix silica sand with water and mix for 1 hour to form a slurry, and control the slurry temperature within the range of 43℃, then add aluminum powder and foam stabilizer to Stir in the slurry for 0.5 minutes, then mix the slurry with well-stirred cement and lime to form a slurry. Control the slurry to stir evenly at a temperature of 43°C until the fluidity of the slurry is controlled at 25-28cm ;

[0029] b. Pour the slurry with a fluidity of 25-28cm into the mold body. Before the slurr...

Embodiment 2

[0033] In the second embodiment, the basic composition of the aerated concrete block of the embodiment is as follows:

[0034] It is made of 300kg cement, 380kg lime, 1500kg silica sand, 150kg aluminum powder, 0.2kg foam stabilizer and water. The foam stabilizer is rosin or bone glue.

[0035] The preparation method of the aerated concrete block according to the above formula includes the following steps in sequence:

[0036] a. Preparation of raw materials: first mix cement and lime uniformly, then mix silica sand and water for 1 hour to form a slurry, and control the slurry temperature within the range of 44℃, then add aluminum powder and foam stabilizer to Stir in the slurry for 0.6 minutes, then mix the slurry with well-stirred cement and lime together to form a slurry. Control the slurry to stir evenly at a temperature of 44°C until the fluidity of the slurry is controlled at 25-28cm ;

[0037] b. Pour the slurry with a fluidity of 25-28cm into the mold body. Before the slurry ...

Embodiment 3

[0041] In the third embodiment, the basic composition of the aerated concrete block of the embodiment is as follows:

[0042] It is made of 320kg cement, 400kg lime, 1600kg silica sand, 1.6kg aluminum powder, 0.205kg foam stabilizer and water. The foam stabilizer is rosin or bone glue.

[0043] The preparation method of the aerated concrete block according to the above formula includes the following steps in sequence:

[0044] a. Preparation of raw materials: first mix cement and lime uniformly, then mix silica sand with water and mix for 1 hour to form a slurry, and control the slurry temperature in the range of 46℃, then add aluminum powder and foam stabilizer to Stir in the slurry for 0.7 minutes, then mix the slurry with the well-stirred cement and lime to form a slurry. Control the slurry to stir evenly at 46°C until the fluidity of the slurry is controlled at 25-28cm ;

[0045] b. Pour the slurry with a fluidity of 25-28cm into the mold body. Before the slurry is poured on the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aerated concrete block and a preparation method thereof. The aerated concrete block is prepared from the following components: 250-320kg of cement, 350-400kg of lime, 1400-1600kg of silica sands, 1.45-1.6kg of aluminium powder, 0.195-0.205kg of foam stabilizers and water. The preparation method comprises the following steps: raw material preparing, metering, stirring, pouring into molds, standing and procuring, demolding, lifting to a cutting part for cutting, steam pressure curing in a kettle and finished product warehousing. The block has the advantages of light weight, good thermal insulation property, processability, convenient construction, wide raw material sources, high preparation efficiency, low preparation energy consumption, environment-friendliness and good fireproofing and soundproofing properties, specifically, the bulk density of the block is 500-700kg / m3, which is equivalent to 1 / 3 of the bulk density of the clay bricks; the block is provided with plentiful pores and micropores inside, thus having good thermal insulation property; the block dispenses with coarse aggregates, thus having good processability, being capable of being sawed, planed, drilled and stapled, being capable of being bonded by bonding materials and providing favorable conditions for building construction.

Description

Technical field [0001] The invention relates to the technical field of manufacturing an autoclaved aerated concrete block, in particular to an autoclaved aerated concrete block and a preparation method thereof. Background technique [0002] An existing Chinese invention patent with the application number CN200910304521.5 titled "A Phosphorus Slag Autoclaved Aerated Concrete Block and Its Preparation Method" discloses an autoclaved aerated concrete block and its preparation method. It is prepared by adding water to phosphorus slag, silica sand, quicklime, cement, gypsum and aluminum powder. Compared with the prior art, this invention uses the waste slag produced in the production of phosphorus as the main material to provide the siliceous component to produce autoclaved aerated concrete blocks, heat preservation, and can produce different levels of autoclaved aerated concrete blocks according to different requirements . While making full use of phosphorous slag waste, it can als...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/10B28B1/14B28B11/24
CPCC04B2111/28C04B28/02
Inventor 王全省
Owner 舟山市宇锦新型墙体材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com