Attapulgite-containing water-based paint for cigarette wrap paper
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of attapulgite and water-based coatings, applied in paper coatings, coatings, papermaking, etc., can solve the problems of cigarette harm reduction and improvement of taste without direct effect, and achieve energy saving, reduction of harmful substances, and simple production process Effect
Active Publication Date: 2012-08-22
YUXI SIRUN PRINTING
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] At present, the function of forming paper is limited to bundling the tow, and has no direct effect on reducing the harm and improving the taste of cigarettes
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0023] A water-based coating for cigarette forming paper containing attapulgite is a product obtained by the following steps:
[0024] A. Add 5g of attapulgite powder into 100g of water, stir and mix to obtain mixed solution a; and
[0025] B. In another container, first heat 100g of water to 80°C, then stir and mix 12g of carboxymethyl cellulose, 8g of tapioca starch, and 8g of guar gum with the 80°C of water to form a cross-linking mixture b; and
[0026] C. Mix the products obtained in the above steps A and B uniformly at a ratio of 2:0.8 to prepare a water-based coating for molding paper.
Embodiment 2
[0028] A water-based coating for cigarette forming paper containing attapulgite is a product obtained by the following steps:
[0029] A, add 20g of attapulgite powder in 100g of water, stir and mix to make mixed solution a; and
[0030] B. In another container, first heat 100g of water to 100°C, then stir and mix 18g of carboxymethyl cellulose, 12g of tapioca starch, and 12g of guar gum with the 100°C of water to form a cross-linking mixture b; and
[0031] C. Mix the products obtained in the above steps A and B uniformly at a ratio of 2:1.5 to prepare a water-based coating for molding paper.
Embodiment 3
[0033] A water-based coating for cigarette forming paper containing attapulgite is a product obtained by the following steps:
[0034] A, add 0.8kg attapulgite powder in 10kg water, stir and mix to make mixed solution a; and
[0035] B. In another container, first heat 10 kg of water to 90° C., then stir and mix 1.4 kg of carboxymethyl cellulose, 1 kg of tapioca starch, and 1 kg of guar gum with the 90° C. water to form a cross-linking mixture b; and
[0036] C. Mix the products obtained in the above steps A and B uniformly at a ratio of 2:1.1 to prepare a water-based coating for molding paper.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides an attapulgite-containing water-based paint for cigarette wrap paper, which can be excellently adhered to wrap paper, can reduce harmful substances in cigarette smoke, and has simple production technology, good safety and no pollution; the water-based paint for wrap paper is prepared by the following technical steps of: adding 5-20 parts of attapulgite powder in 100 parts of water and stirring and mixing the powder and the water to result in mixed solution a; in another vessel, heating 100 parts of water to 80 to 100 DEG C at first, and then stirring and mixing 12-18 parts of carboxymethyl cellulose, 8-12 parts of arrowroot starch, 8-12 parts of guar gum with water at 80 to 100 DEG C to form crosslinking mixed solution b; and mixing the product in the step A with the product in the step B according to the proportion of 2: (0.8-1.5). The attapulgite-containing water-based paint can be excellently adhered to wrap paper and effectively guarantee the adsorption function of the attapulgite in order to reduce harmful substances in cigarette smoke; in addition, the production technology is simple, the cost is low, the problem of residual volatile organic solvent subsequent to coating is avoided due to the use of water as solvent, the energy is saved, the paint is safe and free from pollution, and the cigarette with the paint is safer during smoking.
Description
technical field [0001] The invention belongs to a coating for processed finished paper. Background technique [0002] As we all know, cigarette smoke contains a variety of harmful substances. After smoking, these harmful ingredients deposit in the human body and cause various diseases in the lungs, respiratory tract, stomach and other organs. Although everyone knows that smoking is harmful to health, cigarettes have a refreshing effect. , calming the nerves, proper smoking can excite people, inspire inspiration, and improve work efficiency, so it is still difficult for smokers to quit smoking. As people pay more and more attention to health, the issue of "smoking and health" has been paid more and more attention. harm to the human body. [0003] Attapulgite is a crystalline hydrated magnesium aluminum silicate mineral. It has good colloidal properties such as unique dispersion, high temperature resistance, and salt-alkali resistance, and high adsorption and decolorization ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more