Curable material comprising silylated polymers containing urethane groups, and use thereof in sealants and binders

A urethane group, alkoxysilyl technology for curable materials comprising silylated polymers containing urethane groups and their use in sealants and adhesives field, can solve problems such as low density of silyl groups

Inactive Publication Date: 2011-03-30
EVONIK DEGUSSA GMBH
View PDF28 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a disadvantage is the relatively low density of crosslinkable silyl groups

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Curable material comprising silylated polymers containing urethane groups, and use thereof in sealants and binders
  • Curable material comprising silylated polymers containing urethane groups, and use thereof in sealants and binders
  • Curable material comprising silylated polymers containing urethane groups, and use thereof in sealants and binders

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0266] Working example:

[0267] The following examples were carried out using the following curable materials comprising silyl polyethers 1 containing trialkoxysilyl groups according to the not yet published specification DE 10 2008 000360.3 according to 3-glycidyloxypropyl Triethoxysilane (Dynasylan GLYEO, DMC-catalyzed alkoxylation protocol from Evonik Degussa GmbH). PO stands for propylene oxide.

[0268] To determine polydispersity and average molar mass, GPC determinations were performed under the following conditions: column combination SDV 1000 / 10 000 (length 65cm), temperature 30°C, THF as mobile phase, flow rate 1ml / min, sample concentration 10g / l, RI detector, contrast polypropylene glycol standard evaluation.

[0269] The viscosity was measured at 25° C. according to the method of DIN 53019 using a Brookfield rotational viscometer (type LVT).

[0270] The percentage NCO content is determined according to DIN EN ISO 11909 by back titration with 0.1 molar hydro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

Curable material comprising silylated polymers containing urethane groups, and use thereof in sealants, adhesives, binders and / or surface modifiers.

Description

technical field [0001] The present invention relates to the use of novel curable materials comprising reaction products containing urethane groups and obtainable from silyl polyethers and compounds containing isocyanate groups for surface modification and surface Coatings, for the preparation of sealants, adhesives and adhesives, and for polyurethane systems, the invention also relates to a method for the preparation of said curable material. Background technique [0002] To those skilled in the art, there are many known types of curable materials or reactive prepolymers tailored to the particular field of application. In all cases, the compound needs to contain reactive, curable and / or crosslinkable functional groups, for example, epoxy, amino, hydroxyl, isocyanate, acrylate, vinyl, allyl or silyl group. Among these very different types of prepolymers, moisture-curing systems with silyl groups and / or isocyanate groups are of considerable economic importance. [0003] Amo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/50C08G18/71C08G18/79C08G18/76C08G65/333C09D175/08C08L75/08C04B35/634C03C17/30C08J9/04C09J175/08C09K3/10C09C3/12
CPCC08G65/33348C08G18/792C08G65/336C08G18/10C08G18/0866C08G18/5096C08G65/22C09D175/08C08G18/2825C08G18/755C08G18/718C08G18/289C08G18/307C08G18/3228B32B37/1284B32B37/18B32B37/24B32B2037/243B32B2405/00B32B2581/00C08J9/04C08J2375/08C09D183/06C09J183/06
Inventor F·舒伯特W·克诺特M·费伦茨S·西尔伯
Owner EVONIK DEGUSSA GMBH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap