Antibacterial and low-odor decorative polypropylene material used in saloon car and preparation method thereof

A polypropylene material, low odor technology, applied in the field of antibacterial, low odor polypropylene material for car interior and its preparation, can solve the problems of short validity period and high cost, achieve no secondary pollution, strong sterilization power, and improve antibacterial effect of ability

Active Publication Date: 2013-07-31
CHENGDU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD +3
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, silver ions are directly added to the material, which is easily absorbed by human skin, resulting in short validity period and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial and low-odor decorative polypropylene material used in saloon car and preparation method thereof
  • Antibacterial and low-odor decorative polypropylene material used in saloon car and preparation method thereof
  • Antibacterial and low-odor decorative polypropylene material used in saloon car and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An antibacterial, low-odor polypropylene material for car interiors, which is composed of the following raw materials in weight percentage: polypropylene (brand: AP3N) 60%; elastomer 20%; talcum powder 16%; photocatalytic micropowder 2%; 0.5% antibacterial agent, 0.5% odor absorber, 0.4% antioxidant; 0.3% processing aid; 0.3% white mineral oil.

[0034] The talcum powder mesh number is 3000 mesh. The elastomer is selected from ethylene-octene copolymer. The photocatalytic micropowder is loaded with Ag + TiO 2 . The antibacterial agent is ultrafine ZnO 0.3% and CuO 0.2%. The odor absorbent is 0.3% molecular sieve and 0.2% zeolite. The antioxidants are three (2,4-di-tert-butylphenyl) phenyl phosphite 0.2% and tetrakis (β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid) Pentaerythritol esters 0.2%. Described processing aid is ethylene bis stearamide.

[0035] The preparation method is as follows: (1) firstly add white mineral oil to the mixture of polypropylene ...

Embodiment 2

[0038] An antibacterial, low-odor polypropylene material for car interiors, which is composed of the following raw materials in weight percentage: polypropylene (brand: K7726) 80%; elastomer 5%; talcum powder 10%; photocatalytic micropowder 2%; Antibacterial agent 0.8%, odor absorber 0.7%, antioxidant 0.8%; processing aid 0.5%; white mineral oil 0.2%.

[0039] The talcum powder mesh number is 1250 mesh. The elastomer is selected from ethylene-butene copolymer. The photocatalytic micropowder is loaded with Cu 2+ TiO 2 . The antibacterial agent is Ag 2 O 0.3% and CuO 0.5%. The odor absorbent is 0.4% molecular sieve and 0.3% hydroxyapatite. Described antioxidant is two (2.4-di-tert-butylphenyl) pentaerythritol diphosphite 0.4% and four (beta-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate) pentaerythritol Esters 0.4%. The processing aid is composed of 0.2% ethylene bis stearamide and 0.3% calcium stearate.

[0040] The preparation method is as follows: (1) firstly add whi...

Embodiment 3

[0043] An antibacterial, low-odor polypropylene material for car interiors, consisting of the following raw materials in weight percentage: polypropylene (brand: K7760) 61%; talcum powder 30%; photocatalytic micropowder 5%; antibacterial agent 1.4%, Odor absorbent 1.0%, antioxidant 0.6%; processing aid 0.6%; white mineral oil 0.4%.

[0044] The talcum powder mesh number is 5000 mesh. The photocatalytic micropowder is anatase TiO 2 2% and loaded with Ag + TiO 2 3%. The antibacterial agent is 0.7% of silver-based inorganic antibacterial powder and 0.7% of CuO. The odor absorbing agent is 0.4% of molecular sieve and 0.6% of silicate mineral. The antioxidant is N, N'-bis-(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionyl)hexamethylenediamine 0.3% and tetrakis(β-(3,5 -di-tert-butyl-4-hydroxyphenyl)propionate)pentaerythritol ester 0.3%. The processing aid is composed of 0.3% polyethylene wax and 0.3% calcium stearate.

[0045] The preparation method is as follows: (1) firstly a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial and low-odor decorative polypropylene material used in a saloon car and a preparation method thereof, wherein the material comprises the following components in percentage by weight: 60 to 80 percent of polypropylene, 1 to 20 percent of elastic body, 10 to 30 percent of talcum powder, 1 to 5 percent of photocatalytic micro-powder, 0.5 to 2.0 percent of antibacterial agent, and 0.3 to 1.0 percent of odor absorbent. The polypropylene material can keep low odor enduringly, has antibacterial and mould-proof functions, and has the advantages of strong bactericidal power, quick disinfectant effect, good durability, good stability, no secondary pollution and the like. According to the invention, odorous small molecules such as paraffin, olefins, arenes, amine, phenol, thiol, peroxide, aldehydes, ketones and the like can be effectively removed.

Description

technical field [0001] The invention relates to a modified polypropylene material, in particular to a polypropylene material for antibacterial and low-odor car interior decoration and a preparation method thereof. Background technique [0002] The interior parts of a car generally refer to the partitions of the car compartment, door trim panels, instrument panel assemblies, armrests, carpets and other components. In the past, materials such as metal, wood, and fiber textiles were mostly used for car interior parts, and the appearance and texture were not ideal. With the increasing awareness of environmental protection, some materials that can be recycled, have high material safety performance, and are easy to process are found to replace traditional materials. The materials have become the research and development content of the automobile manufacturing industry in various countries. At present, the interior parts of many cars have gradually used polypropylene (PP) material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/14C08L23/08C08K13/02C08K3/34C08K3/22B29B9/06B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704B29C2948/92895
Inventor 王灿耀黄达罗忠富杨燕李永华吴国峰
Owner CHENGDU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com